Barium-Calcium Ferrite Disc Magnet: 0.09 mol BaCO3 and 0.01 mol CaCO3 (Went, Philips 1956, Ex. 19)
A ceramic magnet with a tenth of the barium replaced by calcium: 0.09 mol barium carbonate and 0.01 mol calcium carbonate to 0.6 mol iron oxide, made as in Example 18: milled, presintered at 1000 °C, milled again, formed and passed through a 1330 °C furnace in 10 minutes. Went's rod held 1,705 gauss with a coercive force of 1,110 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 19. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Hejuru
2 days
Amabwiriza
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 17.76 g barium carbonate (0.09 mol), 1.001 g calcium carbonate (0.01 mol) and 95.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Ibikoresho by'iyi ntambwe:
Karubonate ya bariyumu (witerite)17.76 g
Kaboneti ya kalisiyumu (ifu y'umweru)1.001 g
Oxide ya feri95.55 gIbikoresho bikenewe:
Umunzani w'ibiro
Uturindantoki tw'ikawusu
Agapfukamunwa ka P1002
2
Mill with alcohol 4 hours, dry at 150 °C
Mill with alcohol 4 hours, dry at 150 °C
Grind with alcohol in a ball mill for 4 hours and dry in air at 150 °C.
Ibikoresho bikenewe:
Urusyo rw'imipira y'icyuma
Etanoli - urwego rw'ubushakashatsi, 95 %
Ifuru yo kumishaho3
3
Presinter in air at 1000 °C for 2 hours
Presinter in air at 1000 °C for 2 hours
Fire in air at 1000 °C for 2 hours.
Ibikoresho bikenewe:
Ifuru ya muffle
Ikirundo cyo gushongeramo gifite igifuniko (porukorene)
Amakoro y'Icyombo Gishongesha
Uturindantoki twihanganira ubushyuhe4
4
Mill again 4 hours, dry, form
Mill again 4 hours, dry, form
Grind again with alcohol for 4 hours and dry. Example 19 extrudes a rod; ours: press discs at 1.5 tonnes per cm², as Example 18 moulds its rod.
Ibikoresho bikenewe:
Urusyo rw'imipira y'icyumaEtanoli - urwego rw'ubushakashatsi, 95 %Ifuru yo kumishaho
Imashini ikanda ikoresha amazi
Ifumbiro ryo gukanda disiki5
5
Pass through a 1330 °C zone in 10 minutes
Pass through a 1330 °C zone in 10 minutes
Sinter at 1330 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Ibikoresho bikenewe:
Itanura ry'umuyoboroUturindantoki twihanganira ubushyuhe6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Ibikoresho bikenewe:
Iroha ry'amashanyarazi
IkirangamurongoIbikoresho
3- Umwanya
- Umwanya
- 95.55 gUmwanya
Ibikoresho bikenewe
15- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
Iki gishushanyo gikora
Blueprint zijyanye
Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame
CC0 Umurenge rusange
Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.
Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.