Barium-Calcium Ferrite Disc Magnet: 20 % Calcium, 5 Minutes at 1290 °C (Went, Philips 1956, Ex. 20)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Yaremwe na

Charlie

28. Ukwakira 2026DE
4
0
0
0
0

Barium-Calcium Ferrite Disc Magnet: 20 % Calcium, 5 Minutes at 1290 °C (Went, Philips 1956, Ex. 20)

A ceramic magnet with a fifth of the barium replaced by calcium: 0.08 mol barium carbonate, 0.02 mol calcium carbonate and 0.6 mol iron oxide, made as in Example 18 but sintered at 1290 °C for only 5 minutes. Went's rod held 1,615 gauss with a coercive force of 1,550 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 20. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Hejuru
2 days

Amabwiriza

1

Weigh barium carbonate, chalk and iron oxide

Weigh 15.79 g barium carbonate (0.08 mol), 2.002 g calcium carbonate (0.02 mol) and 95.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Ibikoresho by'iyi ntambwe:

Karubonate ya bariyumu (witerite)Karubonate ya bariyumu (witerite)15.79 g
Kaboneti ya kalisiyumu (ifu y'umweru)Kaboneti ya kalisiyumu (ifu y'umweru)2.002 g
Oxide ya feriOxide ya feri95.55 g

Ibikoresho bikenewe:

Umunzani w'ibiroUmunzani w'ibiro
Uturindantoki tw'ikawusuUturindantoki tw'ikawusu
Agapfukamunwa ka P100Agapfukamunwa ka P100
2

Mill, presinter and mill as in Example 18

As in Example 18: grind with alcohol 4 hours, dry at 150 °C, fire in air at 1000 °C for 2 hours, grind again 4 hours and dry.

Ibikoresho bikenewe:

Urusyo rw'imipira y'icyumaUrusyo rw'imipira y'icyuma
Etanoli - urwego rw'ubushakashatsi, 95 %Etanoli - urwego rw'ubushakashatsi, 95 %
Ifuru yo kumishahoIfuru yo kumishaho
Ifuru ya muffleIfuru ya muffle
Ikirundo cyo gushongeramo gifite igifuniko (porukorene)Ikirundo cyo gushongeramo gifite igifuniko (porukorene)
Amakoro y'Icyombo GishongeshaAmakoro y'Icyombo Gishongesha
3

Press at 1.5 t/cm²

Press at 1.5 tonnes per cm², as in Example 18 (ours: discs instead of rods).

Ibikoresho bikenewe:

Imashini ikanda ikoresha amaziImashini ikanda ikoresha amazi
Ifumbiro ryo gukanda disikiIfumbiro ryo gukanda disiki
4

Pass through a 1290 °C zone in 5 minutes

Sinter in air at 1290 °C by passing the pieces through a 10 cm hot zone at 20 mm per minute: 5 minutes in the heat.

Ibikoresho bikenewe:

Itanura ry'umuyoboroItanura ry'umuyoboro
Uturindantoki twihanganira ubushyuheUturindantoki twihanganira ubushyuhe
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Ibikoresho bikenewe:

Iroha ry'amashanyaraziIroha ry'amashanyarazi
IkirangamurongoIkirangamurongo

Ibikoresho

3

Ibikoresho bikenewe

15

Iki gishushanyo gikora

Thumbnail
Agateganyo

Magineti y'uruziga

Free

11
0
1

Blueprint zijyanye

Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

na CharlieDE

By'Inganda

11
0
0
0
0
0

CC0 Umurenge rusange

Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.

Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.

Ibiganiro

(0)

Injira kugira ngo ujye mu biganiro

Gutegura ibitekerezo...