Barium-Calcium Ferrite Disc Magnet: Equal Barium and Calcium, Sintered at 1280 °C (Went, Philips 1956, Ex. 22)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Yaremwe na

Charlie

28. Ukwakira 2026DE
6
0
0
0
0

Barium-Calcium Ferrite Disc Magnet: Equal Barium and Calcium, Sintered at 1280 °C (Went, Philips 1956, Ex. 22)

A ceramic magnet with equal parts barium and calcium: 0.3 mol barium carbonate, 0.3 mol calcium carbonate and 3.1 mol iron oxide, milled 15 hours, pressed and passed through a 1280 °C furnace in 10 minutes, with no presintering. Went's rod held 1,595 gauss with a coercive force of 1,890 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 22. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Hejuru
2 days

Amabwiriza

1

Weigh barium carbonate, chalk and iron oxide

Weigh 59.5 g barium carbonate (0.3 mol), 30.2 g calcium carbonate (0.3 mol) and 500.0 g ferric oxide (3.1 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Ibikoresho by'iyi ntambwe:

Karubonate ya bariyumu (witerite)Karubonate ya bariyumu (witerite)59.5 g
Kaboneti ya kalisiyumu (ifu y'umweru)Kaboneti ya kalisiyumu (ifu y'umweru)30.2 g
Oxide ya feriOxide ya feri500 g

Ibikoresho bikenewe:

Umunzani w'ibiroUmunzani w'ibiro
Uturindantoki tw'ikawusuUturindantoki tw'ikawusu
Agapfukamunwa ka P100Agapfukamunwa ka P100
2

Mill with alcohol 15 hours, dry, press

Grind with alcohol in a ball mill for 15 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods). No presintering.

Ibikoresho bikenewe:

Urusyo rw'imipira y'icyumaUrusyo rw'imipira y'icyuma
Etanoli - urwego rw'ubushakashatsi, 95 %Etanoli - urwego rw'ubushakashatsi, 95 %
Ifuru yo kumishahoIfuru yo kumishaho
Imashini ikanda ikoresha amaziImashini ikanda ikoresha amazi
Ifumbiro ryo gukanda disikiIfumbiro ryo gukanda disiki
3

Pass through a 1280 °C zone in 10 minutes

Sinter at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Ibikoresho bikenewe:

Itanura ry'umuyoboroItanura ry'umuyoboro
Uturindantoki twihanganira ubushyuheUturindantoki twihanganira ubushyuhe
4

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Ibikoresho bikenewe:

Iroha ry'amashanyaraziIroha ry'amashanyarazi
IkirangamurongoIkirangamurongo

Ibikoresho

3

Ibikoresho bikenewe

12

Iki gishushanyo gikora

Thumbnail
Agateganyo

Magineti y'uruziga

Free

11
0
1

Blueprint zijyanye

Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

na CharlieDE

By'Inganda

11
0
0
0
0
0

CC0 Umurenge rusange

Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.

Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.

Ibiganiro

(0)

Injira kugira ngo ujye mu biganiro

Gutegura ibitekerezo...