Ferrite Toroid Core: Magnesium-Zinc Ferrite Reheated 18 h at 1000 °C and 20 h at 750 °C (Snoek 1948, Ex. III)
Snoek's magnesium-zinc ferrite ring (Example III), fired at 1400 °C and then given a second long treatment in oxygen: 18 hours at 1000 °C and 20 hours at 750 °C. He measured how its losses change with frequency, but gives no permeability for the reheated core.
Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example III. Picture: our diagram.
Hejuru
3 days
Amabwiriza
1
1
Weigh 28 : 18 : 54 mol %
Weigh 28 : 18 : 54 mol %
Mix 28 mol % magnesium oxide, 18 mol % zinc oxide and 54 mol % ferric oxide. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.
Ibikoresho by'iyi ntambwe:
Okiside ya magnesiyumu10.06 g
Ifu ya oxide ya zinki13.06 g
Oxide ya feri76.88 gIbikoresho bikenewe:
Umunzani w'ibiro
Agapfukamunwa k'Umukungugu2
2
Grind 30 hours in an iron mill
Grind 30 hours in an iron mill
Grind the mixture for 30 hours in an iron ball mill.
Ibikoresho bikenewe:
Urusyo rw'imipira y'icyumaAgapfukamunwa k'Umukungugu3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
Ibikoresho bikenewe:
Imashini ikanda ikoresha amazi
Ibumbano ryo gukanda impetaAgapfukamunwa k'Umukungugu4
4
Fire 2 hours at 1400 °C, cool 5–10 °C a minute
Fire 2 hours at 1400 °C, cool 5–10 °C a minute
Heat the ring in oxygen for 2 hours at 1400 °C and cool it slowly in oxygen at 5 to 10 °C per minute.
Ibikoresho bikenewe:
Itanura ry'umuyoboro
Ogisijene
Ibariro rya gazi ifite igitutu
Pirometero
Amakoro y'Icyombo Gishongesha
Uturindantoki twihanganira ubushyuhe5
5
Reheat: 18 hours at 1000 °C, 20 hours at 750 °C
Reheat: 18 hours at 1000 °C, 20 hours at 750 °C
Heat the cooled core to 1000 °C and hold it there for 18 hours, then at 750 °C for 20 hours, and cool slowly again, all in oxygen. Snoek shows the resulting losses only as a curve; he gives no permeability for it.
Ibikoresho bikenewe:
Itanura ry'umuyoboroOgisijeneIbariro rya gazi ifite igitutuPirometeroAmakoro y'Icyombo GishongeshaUturindantoki twihanganira ubushyuheIbikoresho
3- 10.06 gUmwanya
- 13.06 gUmwanya
- 76.88 gUmwanya
Ibikoresho bikenewe
11- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
Iki gishushanyo gikora
Blueprint zijyanye
Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame
CC0 Umurenge rusange
Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.
Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.