Making a Glass Bead on a Mandrel — Lampwork Beadmaking
Forge

Yaremwe na

Forge

26. Gicurasi 2026NO
35
0
0
0
0

Making a Glass Bead on a Mandrel — Lampwork Beadmaking

Lampwork is the art of shaping glass in the flame of a torch or oil lamp. A glass rod is heated until it flows, then wound around a steel mandrel coated in bead release to form a bead. By layering colours, pulling trails, and pressing with simple tools, the beadmaker creates intricate patterns in miniature. Glass beadmaking dates to at least 1500 BCE in Mesopotamia and Egypt, and lampwork beads have been trade goods across every continent. This blueprint covers the core technique of winding a single-colour round bead — the foundation for all lampwork.

Utangiye
1-2 hours

Amabwiriza

1

Set up the torch

Secure a propane or MAPP gas torch to the workbench, angled slightly upward. The flame should be a soft, bushy reducing flame about 10-15 cm long. Work in a well-ventilated area or under a fume hood.

Tools needed:

Propane TorchPropane Torch
2

Prepare the mandrel with bead release

Dip a steel mandrel (a 2-3 mm diameter steel rod) into bead release — a clay-based slurry that prevents the glass from bonding permanently to the steel. Coat about 3 cm of the mandrel tip evenly. Allow to dry completely, then harden in the torch flame briefly.

Materials for this step:

Bead ReleaseBead Release50 ml

Tools needed:

Steel MandrelSteel Mandrel
3

Pre-heat the glass rod

Hold a soda-lime glass rod (5-6 mm diameter) at the edge of the flame and slowly introduce it to the heat. Move it gradually closer over 30 seconds. Sudden heating causes thermal shock — the rod will crack and spit shards.

Materials for this step:

Glass Rod (soda-lime, coloured)Glass Rod (soda-lime, coloured)1 igice
4

Heat the glass to working temperature

Move the rod tip into the hottest part of the flame. The glass will glow orange and begin to flow into a molten ball at the end of the rod. Rotate the rod slowly to keep the gather centred and round.
5

Wind the glass onto the mandrel

Pre-heat the coated section of the mandrel in the flame. Touch the molten glass ball to the mandrel and begin winding — rotate the mandrel steadily while feeding the glass rod. The glass wraps around the mandrel in a spiral. Keep even tension and speed for a uniform bead.
6

Shape the bead in the flame

Once enough glass is wound on, set the glass rod aside. Hold the mandrel in the flame and rotate steadily. Gravity and surface tension will round the bead into a smooth sphere. To make a barrel shape, hold horizontally; for a disc, compress gently with a graphite paddle.
7

Even out the shape

If the bead is lopsided, hold the heavier side downward and let gravity pull it even. For precise shaping, press the bead gently into a graphite marver or use brass shaping tools. Keep the bead rotating to maintain symmetry.
8

Add decorative trails (optional)

For a striped pattern, heat a thin stringer (1-2 mm glass rod) of a contrasting colour and touch it to the rotating hot bead surface. The thin glass trail wraps around the bead. Melt in smooth by returning to the flame, or leave raised for texture.
9

Final flame polish

Hold the finished bead in the flame just long enough for the surface to become glossy and smooth — about 5-10 seconds of gentle rotation. Do not overheat or the bead will distort.
10

Anneal the bead

Place the mandrel with the bead into a pre-heated annealing kiln at approximately 510°C for soda-lime glass. If no kiln is available, bury the bead in vermiculite insulation to slow the cooling. Unannealed beads will crack within hours or days from internal stress.
11

Cool and remove from mandrel

After annealing (at least 1-2 hours in the kiln, or overnight in vermiculite), the bead is cool enough to handle. Soak in water for a few minutes to soften the bead release, then twist and slide the bead off the mandrel. Clean the hole with a pipe cleaner or thin file.
12

Clean and inspect

Rinse the bead under water to remove all bead release residue. Inspect for cracks, bubbles, or uneven shape. A properly made and annealed bead will ring when tapped against another glass bead — a dull thud indicates stress cracks. The bead is now ready for stringing into jewellery.

Ibikoresho

2

Ibikoresho bikenewe

2

Connected Blueprint Materials

Blowing a Glass Vessel on an Iron Pipe — Roman Glassblowing
10% igabana

Blowing a Glass Vessel on an Iron Pipe — Roman Glassblowing

na MaryFI

Glassworking

64
0
0
0
5
0

Blueprint zijyanye

Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame

Blowing a Glass Bottle by Hand — Free-Blown Vessel Shaping

Blowing a Glass Bottle by Hand — Free-Blown Vessel Shaping

na ForgeNO

Glassworking

31
0
0
0
3
0
Making Soda-Lime Glass from Raw Materials — The Recipe That Has Not Changed in 5,000 Years

Making Soda-Lime Glass from Raw Materials — The Recipe That Has Not Changed in 5,000 Years

na MaryFI

Glassworking

54
0
0
0
17
0
Extracting Cobalt from Cobaltite — The Goblin Metal That Colors Glass Blue
Akaga

Extracting Cobalt from Cobaltite — The Goblin Metal That Colors Glass Blue

na PeterSE

Metalworking

47
0
0
0
3
0

CC0 Umurenge rusange

Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.

Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.

Ibiganiro

(0)

Injira kugira ngo ujye mu biganiro

Gutegura ibitekerezo...