Barium Ferrite Disc Magnet: Example 2 Without the Orienting Field (Gorter, Philips 1956, Ex. 2 Comparison)
A ceramic magnet from pre-fired barium ferrite powder suspended in polyvinyl acetate in acetone, made as in Example 2 but without the first, orienting field. Made without the first field, Gorter's comparison block reached a (BH)max of only 0.8 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 2. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Hejuru
3 days
Amabwiriza
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Ibikoresho by'iyi ntambwe:
Karubonate ya bariyumu (witerite)450 g
Oxide ya feri2000 gIbikoresho bikenewe:
Umunzani w'ibiro
Uturindantoki tw'ikawusu
Agapfukamunwa ka P1002
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
Ibikoresho bikenewe:
Urusyo rw'imipira y'icyuma
Etanoli - urwego rw'ubushakashatsi, 95 %
Ifuru yo kumishaho3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
Ibikoresho bikenewe:
Itanura ry'umuyoboro
Ikirundo cyo gushongeramo gifite igifuniko (porukorene)
Uturindantoki twihanganira ubushyuhe4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
Ibikoresho bikenewe:
Urusyo rw'imipira y'icyumaEtanoli - urwego rw'ubushakashatsi, 95 %Ifuru yo kumishaho5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 4 cc of solution per 3 g of powder. The binder burns off later.
Ibikoresho bikenewe:
Polivinili asetate
AsetoneUmunzani w'ibiro6
6
Mould without a first field
Mould without a first field
Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.
Ibikoresho bikenewe:
Ifumbiro ryo gukanda disiki
Imashini ikanda ikoresha amazi7
7
Compress into a block
Compress into a block
Compress the powder into a block. The pressure is not given.
Ibikoresho bikenewe:
Imashini ikanda ikoresha amaziIfumbiro ryo gukanda disiki8
8
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
Ibikoresho bikenewe:
Itanura ry'umuyoboro
Iroha ry'amashanyaraziUturindantoki twihanganira ubushyuhe9
9
Sinter: through a 1300 °C zone in 5 minutes
Sinter: through a 1300 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1300 °C with a 10 cm hot zone: about 5 minutes in the heat.
Ibikoresho bikenewe:
Itanura ry'umuyoboroUturindantoki twihanganira ubushyuhe10
10
Magnetise the block
Magnetise the block
Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.
Ibikoresho bikenewe:
Iroha ry'amashanyarazi
IkirangamurongoIbikoresho
2- Umwanya
- 2000 gUmwanya
Ibikoresho bikenewe
15- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
Iki gishushanyo gikora
Blueprint zijyanye
Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame
CC0 Umurenge rusange
Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.
Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.