Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.1 mol SrCO3 to 0.7 mol Iron Oxide (Went, Philips 1956, Ex. 8)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Yaremwe na

Charlie

28. Ukwakira 2026DE
8
0
0
0
0

Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.1 mol SrCO3 to 0.7 mol Iron Oxide (Went, Philips 1956, Ex. 8)

A strontium ferrite: 0.1 mol strontium carbonate to 0.7 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,535 gauss with a coercive force of 2,800 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 8. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Hejuru
2 days

Amabwiriza

1

Weigh strontium carbonate and iron oxide

Weigh 14.8 g strontium carbonate (0.1 mol) and 112.1 g ferric oxide (0.7 mol).

Ibikoresho by'iyi ntambwe:

Carbonate ya strontiumCarbonate ya strontium14.8 g
Oxide ya feriOxide ya feri112.1 g

Ibikoresho bikenewe:

Umunzani w'ibiroUmunzani w'ibiro
Agapfukamunwa ka P100Agapfukamunwa ka P100
2

Dry at 200 °C, mill with alcohol 4 hours

Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.

Ibikoresho bikenewe:

Ifuru yo kumishahoIfuru yo kumishaho
Urusyo rw'imipira y'icyumaUrusyo rw'imipira y'icyuma
Etanoli - urwego rw'ubushakashatsi, 95 %Etanoli - urwego rw'ubushakashatsi, 95 %
3

Presinter in air at 1100 °C for 3.5 hours

Fire the powder in air at 1100 °C for about 3.5 hours.

Ibikoresho bikenewe:

Ifuru ya muffleIfuru ya muffle
Ikirundo cyo gushongeramo gifite igifuniko (porukorene)Ikirundo cyo gushongeramo gifite igifuniko (porukorene)
Amakoro y'Icyombo GishongeshaAmakoro y'Icyombo Gishongesha
Uturindantoki twihanganira ubushyuheUturindantoki twihanganira ubushyuhe
4

Add a binder and form, dry overnight

Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.

Ibikoresho bikenewe:

Ifu ya polyvinyl alcoholIfu ya polyvinyl alcohol
Imashini ikanda ikoresha amaziImashini ikanda ikoresha amazi
Ifumbiro ryo gukanda disikiIfumbiro ryo gukanda disiki
Ifuru yo kumishahoIfuru yo kumishaho
5

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Ibikoresho bikenewe:

Itanura ry'umuyoboroItanura ry'umuyoboro
Uturindantoki twihanganira ubushyuheUturindantoki twihanganira ubushyuhe
6

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Ibikoresho bikenewe:

Iroha ry'amashanyaraziIroha ry'amashanyarazi
IkirangamurongoIkirangamurongo

Ibikoresho

2

Ibikoresho bikenewe

15

Iki gishushanyo gikora

Thumbnail
Agateganyo

Magineti y'uruziga

Free

11
0
1

Blueprint zijyanye

Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

na CharlieDE

Ibikoresho

11
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

na CharlieDE

Kamere

14
0
0
0
0
0

CC0 Umurenge rusange

Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.

Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.