Metal Oxide Varistor: Zinc Oxide with Bismuth, Manganese and Boric Oxides, 1350 °C (Masuyama 1972, Ex. 3)
Masuyama, Matsuoka and Nishi found that adding two more oxides to zinc oxide and bismuth oxide gives excellent non-linear properties. This is their Example 3 with manganese dioxide and boric oxide: 98.5 % zinc oxide and 0.5 % each of bismuth oxide, manganese dioxide and boric oxide by moles, sintered at 1350 °C. The disc measured a C-value of 101 at 1 mA and a nonlinearity exponent n of 22.2.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 3. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Hejuru
1 day
Amabwiriza
1
1
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide, manganese dioxide and boric oxide 98.5 : 0.5 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.626 g zinc oxide, 0.28 g bismuth oxide, 0.052 g manganese dioxide, 0.042 g boric oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Ibikoresho by'iyi ntambwe:
Ifu ya oxide ya zinki9.626 g
Bisimuti okiside0.28 g
Diyokiside ya manganize (pirolusite)0.052 g
Okiside ya boron0.042 gIbikoresho bikenewe:
Umunzani w'ibiro
Urusyo rw'imipira y'icyuma
Ifuru yo kumishaho2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Ibikoresho bikenewe:
Imashini ikanda ikoresha amazi
Ifumbiro ryo gukanda disiki
Kalipe ya Vernier3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
Ibikoresho bikenewe:
Ifuru ya muffle4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Ibikoresho bikenewe:
Udukombe twa karubide ya silikoniKalipe ya Vernier5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Ibikoresho by'iyi ntambwe:
Igice cya aluminiyumu1 as 3.2 mm spray wire
Irangi rya feza rinyuza amashanyarazi1 as required
Insinga y'Umuringa2 ibiceIbikoresho bikenewe:
Kalipe ya Vernier
Imbunda yo kumisha ukoresheje urumuri rw'insinga
Igikandamiza umwuka cy'ingandaIbikoresho
7- 9.626 gUmwanya
- 0.28 gUmwanya
- Umwanya
- 0.042 gUmwanya
- 1 as 3.2 mm spray wireUmwanya
- 1 as requiredUmwanya
- 2 ibiceUmwanya
Ibikoresho bikenewe
10- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
Iki gishushanyo gikora
Blueprint zijyanye
Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame
CC0 Umurenge rusange
Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.
Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.