Metal Oxide Varistor: Pure Zinc Oxide at 800 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
A varistor made the other way round: a disc of pure zinc oxide, sintered, with bismuth oxide fired into its faces from a paste instead of mixed in. Sintered at 800 °C and fired with the paste at 800 °C, the disc measured a C-value of 300 at 1 mA and a nonlinearity exponent n of 6.8. Masuyama found that firing on the bismuth oxide paste raises n a great deal over mixing it in.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 4. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Hejuru
2 days
Amabwiriza
1
1
Press pure zinc oxide at 340 kg/cm²
Press pure zinc oxide at 340 kg/cm²
Press zinc oxide powder at 340 kg/cm². Example 4 gives no disc size; ours: discs 13 mm across and 2.5 mm thick in the mould of Example 1.
Ibikoresho by'iyi ntambwe:
Ifu ya oxide ya zinki1 as requiredIbikoresho bikenewe:
Umunzani w'ibiro
Imashini ikanda ikoresha amazi
Ifumbiro ryo gukanda disiki
Kalipe ya Vernier2
2
Sinter 1 hour at 800 °C and cool
Sinter 1 hour at 800 °C and cool
Heat the pressed disc for 1 hour at 800 °C, then let it cool to room temperature.
Ibikoresho bikenewe:
Ifuru ya muffle3
3
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 4 gives no thickness.
Ibikoresho bikenewe:
Udukombe twa karubide ya silikoniKalipe ya Vernier4
4
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Ibikoresho by'iyi ntambwe:
Bisimuti okiside1 as requiredIbikoresho bikenewe:
Irembo rya epoxy
n-ButanolIfuru ya muffle5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Ibikoresho by'iyi ntambwe:
Igice cya aluminiyumu1 as 3.2 mm spray wire
Irangi rya feza rinyuza amashanyarazi1 as required
Insinga y'Umuringa2 ibiceIbikoresho bikenewe:
Kalipe ya Vernier
Imbunda yo kumisha ukoresheje urumuri rw'insinga
Igikandamiza umwuka cy'ingandaIbikoresho
5- 1 as requiredUmwanya
- 1 as requiredUmwanya
- 1 as 3.2 mm spray wireUmwanya
- 1 as requiredUmwanya
- 2 ibiceUmwanya
Ibikoresho bikenewe
10- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
Iki gishushanyo gikora
Blueprint zijyanye
Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame
CC0 Umurenge rusange
Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.
Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.