High-Carbon Steel Wire Rod: Billet Hot-Rolled to 9 mm and Coiled
Wire is drawn from rod, and the rod is rolled hot. In a rod mill a steel billet is heated above its recrystallisation temperature and passed through stand after stand of grooved rolls, each one narrower, until it is a round rod about 9 mm thick. The rod is laid in a coil, ready to be cleaned and drawn into wire.
The picture: our diagram, square billet to round rod to coil.
متقدم
Factory process
التعليمات
1
1
Heat the billet
Heat the billet
Heat the high-carbon billet above the steel's recrystallisation temperature.
المواد لهذه الخطوة:
كتلة فولاذ عالي الكربون1 قطعةالأدوات المطلوبة:
سخّان حثّي2
2
Roll through the stands
Roll through the stands
Pass it through the roughing, intermediate and finishing stands of the rod mill. Each pair of grooved rolls makes the section smaller and rounder, down to about 9 mm.
الأدوات المطلوبة:
مدحلة الدرفلة3
3
Keep it hot
Keep it hot
Finish about 50–100 °C above the recrystallisation temperature; reheat if the bar cools below it before the last passes.
الأدوات المطلوبة:
سخّان حثّي4
4
Coil the rod
Coil the rod
Lay the hot rod in loops into a coil and let it cool. It comes out covered in mill scale, which is removed before drawing.
5
5
Rod length from one billet
Rod length from one billet
جارٍ تحميل دفتر Jupyter…
المواد
1- 1 قطعةعنصر نائب
الأدوات المطلوبة
2- عنصر نائب
- عنصر نائب
هذا المخطط يصنع
المخططات ذات الصلة
هذه المخططات تشارك المعرفة مع هذا — التقنيات والمواد والمبادئ
CC0 ملكية عامة
هذا المخطط مُصدر بموجب CC0. يحق لك نسخه وتعديله وتوزيعه واستخدامه لأي غرض، دون طلب إذن.
ادعم الصانع بشراء منتجات عبر مخططه حيث يكسب عمولة الصانع يحددها البائعون، أو أنشئ نسخة جديدة من هذا المخطط وضمّنه كرابط في مخططك لمشاركة الإيرادات.