Nichrome Wire: Nickel and Chromium Fused, Drawn and Annealed

Albert L. Marsh · Public domain (expired patent)

أنشأه

Forge

18. أكتوبر 2026

Nichrome Wire: Nickel and Chromium Fused, Drawn and Annealed

Nichrome is the heating wire of toasters and irons. Albert Marsh patented it in 1906: nickel with less than 25 % chromium, drawn into wire and annealed, with about fifty times the resistance of copper and great resistance to oxidation when hot. Iron, he wrote, will not do. Elwood Haynes (1907) fused pure, carbon-free nickel and chromium in a magnesia crucible under an oxyhydrogen flame. White heat: face shield and gloves. The picture: Marsh's patent drawing, a rheostat wound with the alloy (US 811,859).

متقدم

3 days

التعليمات

Weigh 85 nickel to 15 chromium

Cut 85 g of nickel sheet into small pieces and weigh 15 g of chromium: Marsh's own example. Both must be pure and free of carbon.

المواد لهذه الخطوة:

صفيحة نيكل85 غ

فلز الكروم15 غ

الأدوات المطلوبة:

مقصّ معادن

ميزان ذو كفّتين

Fuse under the oxyhydrogen flame

Put the metals in a magnesia crucible, set it in a furnace lined with magnesia, and heat it with the oxyhydrogen blowpipe until both have melted together.

الأدوات المطلوبة:

بوتقة المغنيسيا

أكسيد المغنيسيوم

مشعل الأكسجين والهيدروجين

ملقط بوتقة

درع للوجه

قفازات جلدية

Cast a rod

Pour the alloy into a narrow mould to get a rod that will start in the largest hole of the drawplate.

الأدوات المطلوبة:

قالب صب السبائك

ملقط بوتقة

درع للوجه

قفازات جلدية

Draw and anneal

Draw the rod down through the drawplate one hole at a time, as in the drawplate blueprint, and anneal it in the furnace whenever it gets hard. Marsh gives no annealing temperature. Stop at 0.41 mm (0.016 in).

الأدوات المطلوبة: