Silicone Rubber Compound: Dimethyl Silicone Oil Gelled with Ferric Oxide, Agens 1948

أنشأه

Mary

17. أكتوبر 2026

Silicone Rubber Compound: Dimethyl Silicone Oil Gelled with Ferric Oxide, Agens 1948

Dimethyl silicone oil mixed with three-quarters its weight of red ferric oxide and a little aluminium chloride, heated to 130 °C, thins and then sets to a solid mass; milled on warm rubber rolls it becomes a silicone rubber compound ready to mould or extrude (Agens, General Electric, US 2,448,756, 1948). Cured, it stretches over 100 % and stays flexible at −60 °C. The picture: our drawing of the beaker, the mill and the sheet.

متقدم

A day

التعليمات

Weigh the mix

To 400 g silicone oil add 300 g ferric oxide (75 % of the oil) and 5 g anhydrous aluminium chloride (1.25 %). Stir it smooth. Keep the chloride dry; it fumes in damp air.

المواد لهذه الخطوة:

زيت سيليكون ثنائي الميثيل400 غ

مسحوق صقل أحمر ناعم300 غ

الأدوات المطلوبة:

كلوريد الألومنيوم (لا مائي)

كأس زجاج بوروسيليكاتي

محرّك تقليب

ميزان مطبخ رقمي

قفازات مطاطية

Heat to 130 °C

Heat the mix to 130 °C. It first gets thinner, then thickens fast until the whole mass is solid.

الأدوات المطلوبة:

صفيحة تسخين

ميزان حرارة

كأس زجاج بوروسيليكاتي

Mill and sheet

Work the mass on rubber rolls at 125 °C for about half an hour and take it off as a sheet. This is the compound.

الأدوات المطلوبة:

خلّاط مطاط ثنائي الأسطوانات

ميزان حرارة

Test a piece

Agens's test: press a sheet about 1.3 mm thick between platens at 150 °C for ten minutes, then 15 minutes in an oven at 200 °C. It should stretch over twice its length.