Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1250 °C, Presintered Once at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered once at 900 °C, pressed into a ring and sintered at 1250 °C in oxygen. Snoek's ring had an initial permeability of 1,230.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
İleri
2 days
Talimatlar
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.
Bu adım için malzemeler:
Bakır Oksit13.24 g
Çinko Oksit Tozu20.32 g
Mor demir oksit66.44 g
Manganez dioksit (pirolusit)1 gGerekli aletler:
Eşit kollu terazi
Toz Maskesi2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
Gerekli aletler:
Demir Bilyalı DeğirmenToz Maskesi3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
Gerekli aletler:
Tüp Fırın
Oksijen
Basınçlı gaz tüpü
Pirometre
Kapaklı kroze (porselen)
Isıya Dayanıklı Eldiven4
4
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
Gerekli aletler:
Demir Bilyalı DeğirmenToz Maskesi5
5
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
Gerekli aletler:
Hidrolik pres
Halka Presleme KalıbıToz Maskesi6
6
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1250 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 1,230, measured at room temperature at 2 kHz.
Gerekli aletler:
Tüp FırınOksijenBasınçlı gaz tüpüPirometre
Pota MaşasıIsıya Dayanıklı EldivenMalzemeler
4- 13.24 gYer Tutucu
- 20.32 gYer Tutucu
- 66.44 gYer Tutucu
- Yer Tutucu
Gerekli Aletler
12- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.