Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This copper-zinc ferrite is milled about 200 hours, fired 2 hours at 1050 °C and held 12 hours at 600 °C; his core had an initial permeability of 200.
The picture: our diagram.
İleri
2 weeks
Talimatlar
1
1
Mix 20 : 30 : 50 mol
Mix 20 : 30 : 50 mol
Mix pure copper oxide, zinc oxide and ferric oxide, 20 : 30 : 50 mol %. Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g ferric oxide per 100 g.
Bu adım için malzemeler:
Bakır Oksit13.24 g
Çinko Oksit Tozu20.32 g
Ferrik oksit66.44 gGerekli aletler:
Eşit kollu terazi
Toz Maskesi2
2
Grind about 200 hours in an iron ball mill
Grind about 200 hours in an iron ball mill
Grind the mixture for about 200 hours in an iron ball mill.
Gerekli aletler:
Demir Bilyalı DeğirmenToz Maskesi3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
Gerekli aletler:
Hidrolik pres
Halka Presleme Kalıbı4
4
Fire 2 hours at 1050 °C, hold 12 hours at 600 °C
Fire 2 hours at 1050 °C, hold 12 hours at 600 °C
Heat the ring for two hours at 1050 °C in a current of oxygen, cool at 5 °C a minute to 600 °C, hold it there 12 hours, then cool to room temperature, all in oxygen. Snoek's core: initial permeability 200.
Gerekli aletler:
Tüp Fırın
Oksijen
Basınçlı gaz tüpü
Pirometre
Pota Maşası
Isıya Dayanıklı EldivenMalzemeler
3- 13.24 gYer Tutucu
- 20.32 gYer Tutucu
- 66.44 gYer Tutucu
Gerekli Aletler
11- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
Tehlikeli
Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Charlie tarafından
Endüstriyel
14
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated
Charlie tarafından
İnorganik
8
0
0
0
0
0
Copper(II) Oxide by Heating Copper in Air
Charlie tarafından
Kimya
23
0
0
0
0
0
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.