Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, Sintered Disc (Masuyama 1972)
A non-linear resistor: the current through it rises far faster than the voltage across it. Masuyama, Matsuoka and Nishi made one from zinc oxide with a little bismuth oxide: pressed into a disc, sintered, lapped, and given metal electrodes. With 0.2 mole % bismuth oxide, sintered at 1000 °C and lapped to 1 mm, the disc measured a C-value of 43 at 1 mA and a nonlinearity exponent n of 4.3.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 1. Unknown: how the aluminium is sprayed on and what the silver paint is. The patent calls both well known, so they are linked to unknown heads. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Просунутий
1 day
Інструкції
1
1
Weigh 99.8 ZnO to 0.2 Bi2O3 and wet-mill 5 hours
Weigh 99.8 ZnO to 0.2 Bi2O3 and wet-mill 5 hours
Mix zinc oxide and bismuth oxide 99.8 : 0.2 by moles. Ours, for 10 g: 9.887 g zinc oxide and 0.113 g bismuth oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Матеріали для цього кроку:
Порошок оксиду цинку9.887 г
Оксид бісмуту0.113 гНеобхідні інструменти ({count})
Важільні терези
Залізний кульовий млин
Сушильна піч2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm².
Необхідні інструменти ({count})
Гідравлічний прес
Прес-форма для дисків
Штангенциркуль3
3
Sinter 1 hour at 1000 °C and furnace-cool
Sinter 1 hour at 1000 °C and furnace-cool
Sinter the discs in air for 1 hour at 1000 °C, then let them cool in the furnace to room temperature (about 15-30 °C). Above 1200 °C the disc loses its nonlinearity.
Необхідні інструменти ({count})
Муфельна піч4
4
Lap both faces to 1.0 mm
Lap both faces to 1.0 mm
Lap both faces with 600-mesh silicon carbide until the disc is 1.0 mm thick.
Необхідні інструменти ({count})
Порошок карбіду кремніюШтангенциркуль5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Unknown: the spraying method and the paint.
Матеріали для цього кроку:
Алюмінієвий зливок1 as required
Срібна струмопровідна фарба1 as required
Мідний дріт2 штукНеобхідні інструменти ({count})
Невідомий спосіб металізації напиленнямШтангенциркульМатеріали
5- 9.887 гЗаповнювач
- 0.113 гЗаповнювач
- 1 as requiredЗаповнювач
- 1 as requiredЗаповнювач
- 2 штукЗаповнювач
Необхідні інструменти
9- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
За цим кресленням виготовляють
Пов'язані креслення
Ці креслення діляться знаннями — техніки, матеріали або принципи
CC0 Суспільне надбання
Це креслення випущено під ліцензією CC0. Ви можете вільно копіювати, змінювати, поширювати та використовувати цю роботу для будь-яких цілей без запиту дозволу.
Підтримайте мейкера, купуючи продукти через його креслення, де він отримує Комісію мейкера встановлену вендорами, або створіть нову ітерацію цього креслення та включіть його як зв'язок у власне креслення для розподілу доходу.