Bone Ash by Calcining Bones
Bone ash is the white material left when bones are calcined: mainly calcium phosphate, generally given as Ca5(OH)(PO4)3, about 56% calcium oxide and 42% phosphorus pentoxide by analysis. It melts only at about 1670 °C. Its porous, high-melting structure makes it the classic cupel for separating silver and gold from lead, and it forms about half of the body of bone china.
Cơ bản
Workshop process
Hướng dẫn
1
1
Clean the bones
Clean the bones
Remove any meat from the bones, then degrease them.
Vật liệu cho bước này:
Xương1 as requiredCông cụ cần thiết:
Dao2
2
Calcine
Calcine
Calcine the bones in a kiln. For bone china they are calcined to around 1000 °C (up to about 1100 °C), which removes all organic matter and leaves the bone sterilised and white; traditional bone ash was calcined lower, at around 800 °C. Most bones keep their cellular structure through calcination. Handle the hot bones with tongs and heat-resistant gloves, and let them cool before grinding.
Công cụ cần thiết:
Lò nung
Kẹp gắp
Găng tay chịu nhiệt3
3
Grind
Grind
Grind the calcined bone with water to a fine particle size, then partially dewater it.
Vật liệu cho bước này:
Nước1 as requiredCông cụ cần thiết:
Cối và chàyBản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.