Electrolytic Iron: Brown Ferrous Electrolyte, Rotating Cathode at 75-77 °C, Graphite Anodes (Bouchayer, US 1,516,326)
Iron plated out of a fresh green ferrous bath comes off rough and useless. Bouchayer first stirred the bath in air until it turned bright brown; the iron oxychloride formed takes care of the hydrogen at the cathode, and the deposit grows even and compact at high current.
Result: electrolytic iron, deposited at about 98 % current yield.
Source: Bouchayer, US 1,516,326 (1924). Not given: cathode material, purity of the iron. Picture drawn by Youblob.
Nâng cao
Factory process
Hướng dẫn
1
1
Make up the electrolyte at 20 °Bé
Make up the electrolyte at 20 °Bé
Dissolve ferrous sulfate in water (Bouchayer also allows ferrous chloride or a mix). Concentration: e.g. 20 °Bé, then keep it constant.
Vật liệu cho bước này:
Sắt sunfat1 as requiredCông cụ cần thiết:
Nước
Tỷ trọng kế
Bể điện phân2
2
Stir it in air until brown
Stir it in air until brown
Agitate the green bath in air, e.g. by turning the anode, until it is bright brown and stops foaming. Used green, it gives only an irregular deposit.
Công cụ cần thiết:
Bể điện phân3
3
Circulate it through iron filings
Circulate it through iron filings
Pump the electrolyte through a mass of iron filings in a separate vessel; it takes back iron and forms the ferric hydroxide that keeps the bath working. Keep it moving fast past the anodes: this lowers the phosphorus.
Vật liệu cho bước này:
Mạt sắt1 as requiredCông cụ cần thiết:
Bơm nước4
4
Deposit on a rotating cathode
Deposit on a rotating cathode
Electrolyse between graphite anodes and a rotating cathode. Temperature: e.g. 75-77 °C at 1000 A/m², held exactly constant and below boiling; cathode speed: e.g. 120 m/min at 800 A/m². Cathode material: not given.
Công cụ cần thiết:
Điện cực graphit
Nguồn điện một chiều
Nhiệt kếBể điện phân5
5
Strip and reheat the deposit
Strip and reheat the deposit
Take the compact iron deposit off the cathode; it is usable after a slight reheating (temperature not given).
Công cụ cần thiết:
Bể điện phânBản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.