Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1250 °C, Presintered Once at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered once at 900 °C, pressed into a ring and sintered at 1250 °C in oxygen. Snoek's ring had an initial permeability of 1,230.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.
Vật liệu cho bước này:
Đồng oxit13.24 g
Bột kẽm oxit20.32 g
Ôxít sắt tím66.44 g
Mangan dioxit (pyrolusit)1 gCông cụ cần thiết:
Cân hai đĩa
Khẩu trang chống bụi2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
Công cụ cần thiết:
Máy nghiền bi sắtKhẩu trang chống bụi3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
Công cụ cần thiết:
Lò ống
Oxy
Bình khí chịu áp suất
Hỏa kế
Chén nung có nắp (sứ)
Găng tay chịu nhiệt4
4
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
Công cụ cần thiết:
Máy nghiền bi sắtKhẩu trang chống bụi5
5
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
Công cụ cần thiết:
Máy ép thủy lực
Khuôn ép vòngKhẩu trang chống bụi6
6
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1250 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 1,230, measured at room temperature at 2 kHz.
Công cụ cần thiết:
Lò ốngOxyBình khí chịu áp suấtHỏa kế
Kìm gắp nồi nấu kim loạiGăng tay chịu nhiệtVật liệu
4- 13.24 gTạm thời
- 20.32 gTạm thời
- 66.44 gTạm thời
- Tạm thời
Công cụ yêu cầu
12- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.