Polypropylene Felt: a Spunbonded Web, Kinney 1967
A polypropylene felt made without weaving or needling: hot filaments are spun, pulled down by an air jet, given an electric charge so they spread apart, and laid in loops on a moving table until they form an even sheet. Kinney's patent (Du Pont, US 3,338,992, 1967) gives every setting for polypropylene. The corona runs at 20 to 25 kV: keep clear of it while it is live.
The picture: the patent's own Fig. 1 (the process) and Fig. 7 (the web).
Nâng cao
1 day
Hướng dẫn
1
1
Melt and spin
Melt and spin
Melt polypropylene of melt index 10 in a screw extruder, no hotter than 290 °C. Meter it at 12 g a minute through a 1/4 in. sand filter and a 20-hole spinneret (holes 0.015 in. across): pack block 275 °C, spinneret 260 °C.
Vật liệu cho bước này:
Hạt nhựa polypropylene500 gCông cụ cần thiết:
Máy đùn nhựa
Đầu phun sợi
Hỏa kế
Cân hai đĩa
Găng tay da2
2
Quench
Quench
Cool the bundle of filaments in a 6 in. quench chimney blowing 40 cubic feet a minute of room air in from the side.
Công cụ cần thiết:
Máy nén khí3
3
Draw with the air jet
Draw with the air jet
Lead the bundle 72 in. down into an air draw jet run at 25 psi: it pulls the filaments with about 3 g of tension and stretches them.
Công cụ cần thiết:
Vòi hút khí kéo sợiMáy nén khí
Đồng hồ áp suất4
4
Charge the filaments
Charge the filaments
8 in. above the jet, let the filaments brush a 1 1/4 in. bar turning at 10 rpm, with a four-point corona 5/8 in. from it at minus 20 to 25 kV (100 to 150 µA). The charge pushes them apart. Keep clear while it is live.
Công cụ cần thiết:
Bộ tích điện corona5
5
Lay the web
Lay the web
Catch the filaments on a grounded 47 in. square table that moves 26 in. a minute one way and 570 in. a minute the other. Each layer weighs 0.5 oz per square yard; lay several for each sheet.
Công cụ cần thiết:
Bàn rải sợi6
6
What you get
What you get
An even sheet of fine filaments, about 2.5 denier each, tenacity 2.0 g per denier, stretching 300 % before they break.
Công cụ cần thiết:
Cân hai đĩaVật liệu
1- Tạm thời
Công cụ yêu cầu
10- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- 1 vendor sell this, none ship to you yetTạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.