Spiegeleisen from Spathic Ore: Siegen Blast Furnace
Spiegeleisen, 'mirror iron', is pig iron rich in manganese. Bessemer steelmakers added it to the blown metal to put back carbon and manganese. The Siegen works made it by roasting their manganese-bearing spathic ore and smelting it in the blast furnace with brown hematite, limestone and coke, as Bauerman describes (1890).
Nâng cao
Works process
Hướng dẫn
1
1
Watch: iron from a blast furnace
Watch: iron from a blast furnace
A 1951 film of the blast furnace: ore, coke and limestone in layers, hot blast, slag and tapping. Spiegeleisen is made the same way from a manganese-rich ore.
2
2
Roast the spathic ore
Roast the spathic ore
Break the ore small. In the kiln, lay 4 in of charcoal on the upper grate, then alternate layers of ore and waste fuel (coke breeze), 40 parts ore to 8 fuel by measure. Light a wood fire on the lower grate and keep it three days. Draw a quarter of the roasted ore each day and refill with half the fuel.
Vật liệu cho bước này:
Quặng sắt spat (siderit)1 as required
Than củi1 as required
Than cốc luyện kim1 as required
Củi1 as requiredCông cụ cần thiết:
Lò nung quặng
Búa tạ3
3
Charge the blast furnace
Charge the blast furnace
Each charge: 28.8 parts roasted spathic ore, 7.2 brown hematite and 9 limestone, with 20 parts coke (Charlottenhütte, by weight).
Vật liệu cho bước này:
Quặng sắt (sắt đầm lầy / hematit / magnetit)1 as required
Canxi cacbonat - đá vôi nghiền1 as requiredThan cốc luyện kim1 as requiredCông cụ cần thiết:
Lò cao4
4
Blow it hot
Blow it hot
Blow through three tuyeres at about 3½ lb per square inch, with a hot blast (280–300° in Bauerman). Keep the hearth hot: a hotter blast reduces more manganese. Keep the slag nearly neutral.
Công cụ cần thiết:
Lò cao
Hỏa kế5
5
Tap and cast
Tap and cast
Tap the metal into moulds. Siegen's spiegeleisen held about 8 % manganese.
Công cụ cần thiết:
Thanh chọc lò
Khuôn đúc thỏi
Găng tay chịu nhiệt
Tấm che mặt6
6
Honest limits
Honest limits
Figures are Bauerman's (1890) for Siegen; a works blast furnace made about 30 tons a day. Later spiegel ran ~15 % manganese (Wikipedia), from richer Spanish and Sardinian ores.
Vật liệu
6- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
Bản thiết kế này làm ra
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.