Two-Part Epoxy Glue: Bis-Phenol Resin Thinned with Allyl Glycidyl Ether, Hardened with Diethylene Triamine
Bis-phenol epoxy resin is too thick to spread, so it is thinned with a fifth of its weight of allyl glycidyl ether, which joins the cure. That is part A; part B is diethylene triamine. Stir 10 parts of B into 100 of A, spread, join, and it hardens at room temperature: after six days at 25 °C, block joints held 3,550 lb/in² (Wiles and Newey, Shell, US 2,528,932, 1950). It bonds wood, metal and resins.
The picture: our drawing of the two bottles and a glued joint.
Trung cấp
A week to full strength
Hướng dẫn
1
1
Make part A
Make part A
Warm 400 g bis-phenol epoxy resin until it flows (our step; it softens at 43 °C) and stir in 100 g allyl glycidyl ether, to a smooth, spreadable syrup. Bottle it.
Vật liệu cho bước này:
Nhựa epoxy bisphenol400 g
Allyl glycidyl ete100 gCông cụ cần thiết:
Cốc thuỷ tinh borosilicat
Bếp điện phẳng
Que khuấy
Nhiệt kế
Cân nhà bếp điện tử
Chai thủy tinh có nắp
Găng tay cao su2
2
Bottle part B
Bottle part B
Bottle diethylene triamine separately and keep it closed: it is strongly alkaline and burns skin. You need 10 g for every 100 g of part A.
Vật liệu cho bước này:
Dietylen triamin50 gCông cụ cần thiết:
Chai thủy tinh có nắpGăng tay cao su3
3
Mix only what you need
Mix only what you need
Weigh part A into a cup, add a tenth of its weight of part B, and stir well. It begins to cure at once, so mix just before gluing.
Công cụ cần thiết:
Cốc đongCân nhà bếp điện tửQue khuấyGăng tay cao su4
4
Spread, join, wait
Spread, join, wait
Spread a thin coat on both faces and press them together. At room temperature it sets in half an hour to a day and reaches full strength in one to two weeks; warmth speeds it up.
Công cụ cần thiết:
Chổi quét keo5
5
Mixing table
Mixing table
Đang tải sổ tay Jupyter…
Vật liệu
3- 400 gTạm thời
- 100 gTạm thời
- 50 gTạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
Nguy hiểm
Bisphenol Epoxy Resin: Bisphenol A and Epichlorohydrin in Caustic Soda, Wiles and Newey 1950
bởi Charlie
Polyme
9
0
0
0
0
0
Nguy hiểm
Allyl Glycidyl Ether: Allyl Alcohol and Epichlorohydrin, Evans, Marple and Shokal 1943
bởi Charlie
Hữu cơ
16
0
0
0
0
0
Nguy hiểm
Ethylene Amines: Ethylene Dichloride Heated with Ammonia Water, Mnookin 1936
bởi Charlie
Hữu cơ
12
0
0
0
0
0
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.