Metal Oxide Varistor: Zinc Oxide with 2.5 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 97.5 % zinc oxide with 2.5 % manganese dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 177 at 1 mA and a nonlinearity exponent n of 6.8.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh 97.5 : 2.5 and wet-mill 5 hours
Weigh 97.5 : 2.5 and wet-mill 5 hours
Mix zinc oxide and manganese dioxide 97.5 : 2.5 by moles. Ours, for 10 g: 9.733 g zinc oxide and 0.267 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Vật liệu cho bước này:
Bột kẽm oxit9.733 g
Mangan dioxit (pyrolusit)0.267 gCông cụ cần thiết:
Cân hai đĩa
Máy nghiền bi sắt
Lò sấy2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Công cụ cần thiết:
Máy ép thủy lực
Khuôn ép đĩa
Thước cặp3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Công cụ cần thiết:
Lò muffle4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Công cụ cần thiết:
Hạt mài cacbua silicThước cặp5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Vật liệu cho bước này:
Oxit bitmut1 as requiredCông cụ cần thiết:
Nhựa epoxy
n-ButanolLò muffle6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Vật liệu cho bước này:
Thỏi nhôm1 as 3.2 mm spray wire
Sơn bạc dẫn điện1 as required
Dây đồng2 cáiCông cụ cần thiết:
Thước cặp
Súng phun hồ quang dây
Máy nén khí công nghiệpVật liệu
6- 9.733 gTạm thời
- 0.267 gTạm thời
- 1 as requiredTạm thời
- 1 as 3.2 mm spray wireTạm thời
- 1 as requiredTạm thời
- 2 cáiTạm thời
Công cụ yêu cầu
12- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.