Metal Oxide Varistor: Zinc Oxide with 0.5 % Chromic Oxide, Bismuth-Manganese Oxide Paste Fired On (Masuyama 1972, Ex. 7)
A varistor whose bismuth oxide and manganese dioxide are both fired on from a paste: 99.5 % zinc oxide with 0.5 % chromic oxide by moles, sintered at 1350 °C, coated with a 70 : 30 bismuth oxide and manganese dioxide paste and fired at 800 °C. The disc measured a C-value of 167 at 1 mA and a nonlinearity exponent n of 34.2.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 7. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh 99.5 : 0.5 and wet-mill 5 hours
Weigh 99.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide and chromic oxide 99.5 : 0.5 by moles. Ours, for 10 g: 9.907 g zinc oxide, 0.093 g chromic oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Vật liệu cho bước này:
Bột kẽm oxit9.907 g
Oxit crom0.093 gCông cụ cần thiết:
Cân hai đĩa
Máy nghiền bi sắt
Lò sấy2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Công cụ cần thiết:
Máy ép thủy lực
Khuôn ép đĩa
Thước cặp3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Công cụ cần thiết:
Lò muffle4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 7 gives no thickness.
Công cụ cần thiết:
Hạt mài cacbua silicThước cặp5
5
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat both lapped faces with a paste whose solids are 70 % bismuth oxide and 30 % manganese dioxide by weight, and fire it in air at 800 °C for 30 minutes. Example 7 does not name the paste's liquid; ours: the epoxy-resin butyl-alcohol solution of Example 4. Not given: how much paste.
Vật liệu cho bước này:
Oxit bitmut1 as required
Mangan dioxit (pyrolusit)1 as requiredCông cụ cần thiết:
Nhựa epoxy
n-ButanolLò muffle6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Vật liệu cho bước này:
Thỏi nhôm1 as required
Sơn bạc dẫn điện1 as required
Dây đồng2 cáiCông cụ cần thiết:
Phương pháp phun kim loại chưa biếtThước cặpVật liệu
7- 9.907 gTạm thời
- 0.093 gTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 1 as requiredTạm thời
- 2 cáiTạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.