Ferrite Toroid Core: Wet-Process Copper-Zinc Ferrite with a Stepped Anneal Down to 310 °C (Snoek 1948)
The wet-process copper-zinc ferrite ring of Snoek's Example II, given a long stepped anneal in oxygen after its 600 °C hold: 19 hours at 510 °C, 34 hours at 410 °C and 12 hours at 310 °C. The initial permeability fell from 500 to 410.
Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
Osezingeni eliphezulu
3 days
Imiyalelo
1
1
Dissolve the copper, zinc and iron salts
Dissolve the copper, zinc and iron salts
Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.
Izinto zokwakha zalesi sinyathelo:
I-copper sulfate pentahydrate (CuSO4·5H2O)49.94 g
I-zinc sulfate0.3 mol
I-ferric nitrate1 mol
Amanzi Acwengisisiwe1 lAmathuluzi adingekayo:
Isikali sesilinganiso
Ibhikha Le-borosilicate
Amagilavu erabha2
2
Precipitate hot with 9 M caustic soda
Precipitate hot with 9 M caustic soda
Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.
Izinto zokwakha zalesi sinyathelo:
I-Sodium Hydroxide — izinga laselabhorethri180 gAmathuluzi adingekayo:
Ibhikha Le-borosilicate
Ipuleti Elishisayo
Izibuko Zokuchitheka KwamakhemikhaliAmagilavu erabha3
3
Wash, dry and pre-heat at 700 °C
Wash, dry and pre-heat at 700 °C
Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.
Amathuluzi adingekayo:
Iphepha LokuhluzaAmanzi Acwengisisiwe
Ihhavini yokomisa
Isithando Sepayipi
I-crucible enesivalo (i-porcelain)
Amagilavu Amelana Nokushisa4
4
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
Amathuluzi adingekayo:
Umshini wokucindezela we-hydraulic
Isikhunta Sokucindezela Izindandatho
Imaski Yothuli5
5
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.
Amathuluzi adingekayo:
Isithando Sepayipi
I-oxygen
Isilinda segesi ecindezelwe
I-pyrometer
Udlawu Lwesitsha SokuncibilikisaAmagilavu Amelana Nokushisa6
6
Anneal 19 h at 510 °C, 34 h at 410 °C, 12 h at 310 °C
Anneal 19 h at 510 °C, 34 h at 410 °C, 12 h at 310 °C
After the 600 °C hold, keep the core for another 19 hours at 510 °C, 34 hours at 410 °C and 12 hours at 310 °C, all in oxygen. Snoek's core: initial permeability 410.
Amathuluzi adingekayo:
Isithando SepayipiI-oxygenIsilinda segesi ecindezelweI-pyrometerUdlawu Lwesitsha SokuncibilikisaAmagilavu Amelana NokushisaIzinto
5- Isibambeli
- 0.3 molIsibambeli
- 1 molIsibambeli
- Isibambeli
- Isibambeli
Amathuluzi Adingekayo
18- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
- Isibambeli
Le blueprint yenza
Ama-blueprint ahlobene
Lama-blueprint abelana ngolwazi — amasu, izinto noma izimiso
CC0 Isizinda Somphakathi
Le blueprint ikhishwe ngaphansi kwe-CC0. Ukhululekile ukukopisha, ukuguqula, ukusabalalisa, nokusebenzisa ngaphandle kwemvume.
Sekela uMenzi ngokuthenga imikhiqizo nge-Blueprint yabo IKhomishane Yomenzi kumiswe ngabathengisi, noma dala inguqulo entsha yale Blueprint bese uyifaka njengoxhumaniso ku-Blueprint yakho ukuze wabelane ngemali engenayo.