Barium-Calcium Ferrite Disc Magnet: Part of the Barium Replaced by Calcium (Went, Philips 1956, Ex. 21)
A ceramic magnet in which part of the barium is replaced by calcium: 0.06 mol barium carbonate and 0.04 mol calcium carbonate to 0.6 mol iron oxide, milled, fired in oxygen, milled again, pressed and passed quickly through a hot furnace. Went's rod held 1,660 gauss with a coercive force of 1,210 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 21. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avançado
2 days
Instruções
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 11.84 g barium carbonate (0.06 mol), 4.004 g calcium carbonate (0.04 mol) and 99.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Materiais para este passo:
Carbonato de bário (witherita)11.84 g
Carbonato de cálcio (branco de espanha)4.004 g
Óxido férrico99.55 gFerramentas necessárias:
Balança de pratos
Luvas de borracha
Respirador P1002
2
Mill with alcohol 4 hours and dry
Mill with alcohol 4 hours and dry
Grind the mixture with alcohol in a ball mill for 4 hours, then dry it.
Ferramentas necessárias:
Moinho de bolas de ferro
Etanol de laboratório, 95 %
Estufa de secagem3
3
Presinter in oxygen at 1000 °C for 2 hours
Presinter in oxygen at 1000 °C for 2 hours
Fire the dry powder in oxygen at 1000 °C for 2 hours (ours: a tube furnace fed from an oxygen cylinder).
Ferramentas necessárias:
Forno tubular
Oxigénio
Garrafa de gás sob pressão
Luvas resistentes ao calor4
4
Mill again 4 hours, dry, press at 1.5 t/cm²
Mill again 4 hours, dry, press at 1.5 t/cm²
Grind with alcohol in the ball mill for 4 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods).
Ferramentas necessárias:
Moinho de bolas de ferroEtanol de laboratório, 95 %Estufa de secagem
Prensa hidráulica
Matriz de prensagem de discos5
5
Pass through a 1200 °C zone in 10 minutes
Pass through a 1200 °C zone in 10 minutes
Sinter at 1200 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute, which is 10 minutes in the heat.
Ferramentas necessárias:
Forno tubularLuvas resistentes ao calor6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Ferramentas necessárias:
Eletroíman
BússolaMateriais
3- Referência
- Referência
- 99.55 gReferência
Ferramentas necessárias
14- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
Este projeto faz
Blueprints relacionados
Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios
CC0 Domínio Público
Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.
Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.