Barium Ferrite Disc Magnet: 1 mol BaCO3 to 2.5 mol Iron Oxide, 1310 °C (Went, Philips 1956, Ex. 1)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Criado por

Charlie

28. outubro 2026DE
0
0
0
0
0

Barium Ferrite Disc Magnet: 1 mol BaCO3 to 2.5 mol Iron Oxide, 1310 °C (Went, Philips 1956, Ex. 1)

Went's first barium ferrite: 1 mol barium carbonate to 2.5 mol iron oxide, milled 13.5 hours, bound, formed and passed through a 1310 °C furnace in 20 minutes. His rod held 1,200 gauss with a coercive force of 1,940 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 1. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avançado
2 days

Instruções

1

Weigh barium carbonate and iron oxide

Weigh 201.1 g barium carbonate (1 mol) and 400.5 g ferric oxide (2.5 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Materiais para este passo:

Carbonato de bário (witherita)Carbonato de bário (witherita)201.1 g
Óxido férricoÓxido férrico400.5 g

Ferramentas necessárias:

Balança de pratosBalança de pratos
Luvas de borrachaLuvas de borracha
Respirador P100Respirador P100
2

Mill with alcohol 13.5 hours, dry and sieve

Grind the mixture with alcohol in a ball mill for 13.5 hours, then dry it and sieve it.

Ferramentas necessárias:

Moinho de bolas de ferroMoinho de bolas de ferro
Etanol de laboratório, 95 %Etanol de laboratório, 95 %
Estufa de secagemEstufa de secagem
CrivoCrivo
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Ferramentas necessárias:

Álcool polivinílico em póÁlcool polivinílico em pó
Prensa hidráulicaPrensa hidráulica
Matriz de prensagem de discosMatriz de prensagem de discos
Estufa de secagemEstufa de secagem
4

Pass through a 1310 °C zone in 20 minutes

Sinter in air at 1310 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.

Ferramentas necessárias:

Forno tubularForno tubular
Luvas resistentes ao calorLuvas resistentes ao calor
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Ferramentas necessárias:

EletroímanEletroíman
BússolaBússola

Materiais

2

Ferramentas necessárias

14

Este projeto faz

Thumbnail
Espaço reservado

Ímã de disco

Free

0
0
1

Blueprints relacionados

Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

por CharlieDE

Industrial

0
0
0
0
0
0

CC0 Domínio Público

Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.

Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.

Discussão

(0)

Entrar para participar da discussão

Carregando comentários...