Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this copper-zinc ferrite ring at a lower heat: technical copper oxide, zinc oxide and iron oxide with 1 % brownstone, fired at 1050 °C, then held 14 hours at 600 °C, all in oxygen. His ring had an initial permeability of 385.
The picture: our diagram.
Avançado
2 days
Instruções
1
1
Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone
Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone
Mix technical copper oxide, zinc oxide and iron oxide in the molecular ratio 20.7 : 31.6 : 47.7 (on the pure oxides) and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.91 g copper oxide, 21.73 g zinc oxide and 64.36 g ferric oxide per 100 g, plus 1 g brownstone.
Materiais para este passo:
Óxido de cobre13.91 g
Óxido de zinco em pó21.73 g
Óxido férrico64.36 g
Dióxido de manganês (pirolusite)1 gFerramentas necessárias:
Balança de pratos
Máscara antipoeiras2
2
Grind for 3 hours in an iron ball mill
Grind for 3 hours in an iron ball mill
Grind the mixture for 3 hours in a mill with iron balls.
Ferramentas necessárias:
Moinho de bolas de ferroMáscara antipoeiras3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.
Ferramentas necessárias:
Prensa hidráulica
Matriz de prensagem de anéis
Água destilada4
4
Fire 1 hour at 1050 °C, hold 14 hours at 600 °C
Fire 1 hour at 1050 °C, hold 14 hours at 600 °C
Sinter the ring in oxygen at 1050 °C for 1 hour, cool it slowly to 600 °C and hold it there for 14 hours, all in oxygen, then let it cool further. Snoek's core had an initial permeability of 385.
Ferramentas necessárias:
Forno tubular
Oxigénio
Garrafa de gás sob pressão
Pirómetro
Tenaz para cadinho
Luvas resistentes ao calorMateriais
4- 13.91 gReferência
- 21.73 gReferência
- 64.36 gReferência
- Referência
Ferramentas necessárias
12- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
Este projeto faz
Blueprints relacionados
Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios
CC0 Domínio Público
Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.
Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.