Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, 1000 °C, 1.5 mm (Masuyama 1972)
A non-linear resistor: the current through it rises far faster than the voltage across it. Masuyama, Matsuoka and Nishi made one from zinc oxide with a little bismuth oxide: pressed into a disc, sintered, lapped, and given metal electrodes. With 0.2 mole % bismuth oxide, sintered at 1000 °C and lapped to 1.5 mm, the disc measured a C-value of 65 at 1 mA and a nonlinearity exponent n of 4.3.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 1. Unknown: how the aluminium is sprayed on and what the silver paint is. The patent calls both well known, so they are linked to unknown heads. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Avançado
1 day
Instruções
1
1
Weigh 99.8 : 0.2 and wet-mill 5 hours
Weigh 99.8 : 0.2 and wet-mill 5 hours
Mix zinc oxide and bismuth oxide 99.8 : 0.2 by moles. Ours, for 10 g: 9.887 g zinc oxide, 0.113 g bismuth oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Materiais para este passo:
Óxido de zinco em pó9.887 g
Óxido de bismuto0.113 gFerramentas necessárias:
Balança de pratos
Moinho de bolas de ferro
Estufa de secagem2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm².
Ferramentas necessárias:
Prensa hidráulica
Matriz de prensagem de discos
Paquímetro3
3
Sinter 1 hour at 1000 °C and furnace-cool
Sinter 1 hour at 1000 °C and furnace-cool
Sinter the discs in air for 1 hour at 1000 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
Ferramentas necessárias:
Forno mufla4
4
Lap both faces to 1.5 mm
Lap both faces to 1.5 mm
Lap both faces with 600-mesh silicon carbide until the disc is 1.5 mm thick.
Ferramentas necessárias:
Grão de carboneto de silícioPaquímetro5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Unknown: the spraying method and the paint.
Materiais para este passo:
Lingote de alumínio1 as required
Tinta condutora de prata1 as required
Fio de cobre2 peçasFerramentas necessárias:
Método de metalização por aspersão desconhecidoPaquímetroMateriais
5- 9.887 gReferência
- 0.113 gReferência
- 1 as requiredReferência
- 1 as requiredReferência
- 2 peçasReferência
Ferramentas necessárias
9- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
Blueprints relacionados
Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios
CC0 Domínio Público
Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.
Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.