Metal Oxide Varistor: Zinc Oxide with Bismuth, Manganese and Boric Oxides, 1350 °C (Masuyama 1972, Ex. 3)
Masuyama, Matsuoka and Nishi found that adding two more oxides to zinc oxide and bismuth oxide gives excellent non-linear properties. This is their Example 3 with manganese dioxide and boric oxide: 98.5 % zinc oxide and 0.5 % each of bismuth oxide, manganese dioxide and boric oxide by moles, sintered at 1350 °C. The disc measured a C-value of 101 at 1 mA and a nonlinearity exponent n of 22.2.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 3. Unknown: how the aluminium is sprayed on and what the silver paint is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Avançado
1 day
Instruções
1
1
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide, manganese dioxide and boric oxide 98.5 : 0.5 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.626 g zinc oxide, 0.28 g bismuth oxide, 0.052 g manganese dioxide, 0.042 g boric oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Materiais para este passo:
Óxido de zinco em pó9.626 g
Óxido de bismuto0.28 g
Dióxido de manganês (pirolusite)0.052 g
Óxido bórico0.042 gFerramentas necessárias:
Balança de pratos
Moinho de bolas de ferro
Estufa de secagem2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Ferramentas necessárias:
Prensa hidráulica
Matriz de prensagem de discos
Paquímetro3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
Ferramentas necessárias:
Forno mufla4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Ferramentas necessárias:
Grão de carboneto de silícioPaquímetro5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Unknown: the spraying method and the paint.
Materiais para este passo:
Lingote de alumínio1 as required
Tinta condutora de prata1 as required
Fio de cobre2 peçasFerramentas necessárias:
Método de metalização por aspersão desconhecidoPaquímetroMateriais
7- 9.626 gReferência
- 0.28 gReferência
- Referência
- 0.042 gReferência
- 1 as requiredReferência
- 1 as requiredReferência
- 2 peçasReferência
Ferramentas necessárias
9- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
Blueprints relacionados
Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios
CC0 Domínio Público
Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.
Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.