Metal Oxide Varistor: Zinc Oxide with 1 % Aluminium Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 99 % zinc oxide with 1 % aluminium oxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 6.2 at 1 mA and a nonlinearity exponent n of 7.4.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Avançado
2 days
Instruções
1
1
Weigh 99 : 1 and wet-mill 5 hours
Weigh 99 : 1 and wet-mill 5 hours
Mix zinc oxide and aluminium oxide 99 : 1 by moles. Ours, for 10 g: 9.875 g zinc oxide and 0.125 g aluminium oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Materiais para este passo:
Óxido de zinco em pó9.875 g
Pó de alumina (óxido de alumínio)0.125 gFerramentas necessárias:
Balança de pratos
Moinho de bolas de ferro
Estufa de secagem2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Ferramentas necessárias:
Prensa hidráulica
Matriz de prensagem de discos
Paquímetro3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Ferramentas necessárias:
Forno mufla4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Ferramentas necessárias:
Grão de carboneto de silícioPaquímetro5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Materiais para este passo:
Óxido de bismuto1 as requiredFerramentas necessárias:
Resina epóxi
n-ButanolForno mufla6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Materiais para este passo:
Lingote de alumínio1 as required
Tinta condutora de prata1 as required
Fio de cobre2 peçasFerramentas necessárias:
Método de metalização por aspersão desconhecidoPaquímetroMateriais
6- 9.875 gReferência
- Referência
- 1 as requiredReferência
- 1 as requiredReferência
- 1 as requiredReferência
- 2 peçasReferência
Ferramentas necessárias
11- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
Blueprints relacionados
Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios
CC0 Domínio Público
Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.
Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.