Metal Oxide Varistor: Zinc Oxide with 0.5 % Barium Oxide, Bismuth-Manganese Oxide Paste Fired On (Masuyama 1972, Ex. 7)
A varistor whose bismuth oxide and manganese dioxide are both fired on from a paste: 99.5 % zinc oxide with 0.5 % barium oxide by moles, sintered at 1350 °C, coated with a 70 : 30 bismuth oxide and manganese dioxide paste and fired at 800 °C. The disc measured a C-value of 77 at 1 mA and a nonlinearity exponent n of 43.1.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 7. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Avançado
2 days
Instruções
1
1
Weigh 99.5 : 0.5 and wet-mill 5 hours
Weigh 99.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide and barium oxide 99.5 : 0.5 by moles. Ours, for 10 g: 9.906 g zinc oxide, 0.094 g barium oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Materiais para este passo:
Óxido de zinco em pó9.906 g
Óxido de bário0.094 gFerramentas necessárias:
Balança de pratos
Moinho de bolas de ferro
Estufa de secagem2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Ferramentas necessárias:
Prensa hidráulica
Matriz de prensagem de discos
Paquímetro3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Ferramentas necessárias:
Forno mufla4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 7 gives no thickness.
Ferramentas necessárias:
Grão de carboneto de silícioPaquímetro5
5
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat both lapped faces with a paste whose solids are 70 % bismuth oxide and 30 % manganese dioxide by weight, and fire it in air at 800 °C for 30 minutes. Example 7 does not name the paste's liquid; ours: the epoxy-resin butyl-alcohol solution of Example 4. Not given: how much paste.
Materiais para este passo:
Óxido de bismuto1 as required
Dióxido de manganês (pirolusite)1 as requiredFerramentas necessárias:
Resina epóxi
n-ButanolForno mufla6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Materiais para este passo:
Lingote de alumínio1 as required
Tinta condutora de prata1 as required
Fio de cobre2 peçasFerramentas necessárias:
Método de metalização por aspersão desconhecidoPaquímetroMateriais
7- 9.906 gReferência
- 0.094 gReferência
- 1 as requiredReferência
- 1 as requiredReferência
- 1 as requiredReferência
- 1 as requiredReferência
- 2 peçasReferência
Ferramentas necessárias
11- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
- Referência
Blueprints relacionados
Estes blueprints compartilham conhecimento — técnicas, materiais ou princípios
CC0 Domínio Público
Este blueprint é liberado sob CC0. Você é livre para copiar, modificar, distribuir e usar este trabalho para qualquer finalidade, sem pedir permissão.
Apoie o Maker comprando produtos através do Blueprint, onde ele ganha uma Comissão Maker definida pelos vendedores, ou crie uma nova versão deste Blueprint e inclua-o como conexão no seu próprio Blueprint para compartilhar receita.