Metal Oxide Varistor: Zinc Oxide with 0.5 % Boric Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
von Ed
Industriell
6
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.5 % Titanium Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.5 % Nickel Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
von Ed
Industriell
8
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.5 % Barium Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
von Ed
Industriell
3
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.5 % Tin Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.5 % Antimony Trioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1350 °C, Bismuth Oxide Paste Fired at 1300 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
5
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1350 °C, Bismuth Oxide Paste Fired at 1200 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
3
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1350 °C, Bismuth Oxide Paste Fired at 1000 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1350 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
5
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1350 °C, Bismuth Oxide Paste Fired at 600 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1400 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1300 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1150 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
2
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 1000 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
1
0
0
0
0
0
Metal Oxide Varistor: Pure Zinc Oxide at 800 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
von Ed
Industriell
5
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with Bismuth, Manganese and Boric Oxides, 1350 °C (Masuyama 1972, Ex. 3)
von Ed
Industriell
2
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.5 % Ferric Oxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
4
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.5 % Boric Oxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
3
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 12 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
2
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 2.5 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
2
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.2 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
3
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.05 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
3
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.03 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
von Ed
Industriell
7
0
0
0
0
0