Barium-Calcium Ferrite Disc Magnet: Part of the Barium Replaced by Calcium (Went, Philips 1956, Ex. 21)
A ceramic magnet in which part of the barium is replaced by calcium: 0.06 mol barium carbonate and 0.04 mol calcium carbonate to 0.6 mol iron oxide, milled, fired in oxygen, milled again, pressed and passed quickly through a hot furnace. Went's rod held 1,660 gauss with a coercive force of 1,210 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 21. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avancé
2 days
Consignes
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 11.84 g barium carbonate (0.06 mol), 4.004 g calcium carbonate (0.04 mol) and 99.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Matériaux pour cette étape :
Carbonate de baryum (withérite)11.84 g
Carbonate de calcium (blanc de Meudon)4.004 g
Oxyde ferrique99.55 gOutils nécessaires :
Balance à fléau
Gants en caoutchouc
Masque respiratoire P1002
2
Mill with alcohol 4 hours and dry
Mill with alcohol 4 hours and dry
Grind the mixture with alcohol in a ball mill for 4 hours, then dry it.
Outils nécessaires :
Broyeur à boulets de fer
Éthanol de laboratoire, 95 %
Étuve de séchage3
3
Presinter in oxygen at 1000 °C for 2 hours
Presinter in oxygen at 1000 °C for 2 hours
Fire the dry powder in oxygen at 1000 °C for 2 hours (ours: a tube furnace fed from an oxygen cylinder).
Outils nécessaires :
Four tubulaire
Oxygène
Bouteille de gaz sous pression
Gants résistants à la chaleur4
4
Mill again 4 hours, dry, press at 1.5 t/cm²
Mill again 4 hours, dry, press at 1.5 t/cm²
Grind with alcohol in the ball mill for 4 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods).
Outils nécessaires :
Broyeur à boulets de ferÉthanol de laboratoire, 95 %Étuve de séchage
Presse hydraulique
Matrice de pressage de disques5
5
Pass through a 1200 °C zone in 10 minutes
Pass through a 1200 °C zone in 10 minutes
Sinter at 1200 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute, which is 10 minutes in the heat.
Outils nécessaires :
Four tubulaireGants résistants à la chaleur6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Outils nécessaires :
Électroaimant
BoussoleMatériaux
3- Espace réservé
- Espace réservé
- 99.55 gEspace réservé
Outils requis
14- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
Ce plan fabrique
Blueprints liés
Ces blueprints partagent des connaissances — techniques, matériaux ou principes
CC0 Domaine public
Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.
Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.