Barium Ferrite Disc Magnet: Example 7 Without the Orienting Field (Gorter, Philips 1956, Ex. 7 Comparison)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Créé par

Charlie

28. octobre 2026DE
3
0
0
0
0

Barium Ferrite Disc Magnet: Example 7 Without the Orienting Field (Gorter, Philips 1956, Ex. 7 Comparison)

Made as in Example 7 but without the first, orienting field. Gorter's comparison blocks held 2,250 gauss with a coercive force of 1,850 oersted and a (BH)max of 0.95 × 10⁶. Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 7. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avancé
3 days

Consignes

1

Weigh barium carbonate and iron oxide

Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Matériaux pour cette étape :

Carbonate de baryum (withérite)Carbonate de baryum (withérite)450 g
Oxyde ferriqueOxyde ferrique2000 g

Outils nécessaires :

Balance à fléauBalance à fléau
Gants en caoutchoucGants en caoutchouc
Masque respiratoire P100Masque respiratoire P100
2

Mill 20 hours under alcohol, dry

Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.

Outils nécessaires :

Broyeur à boulets de ferBroyeur à boulets de fer
Éthanol de laboratoire, 95 %Éthanol de laboratoire, 95 %
Étuve de séchageÉtuve de séchage
3

Pre-fire: through a 1100 °C zone in 10 minutes

Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.

Outils nécessaires :

Four tubulaireFour tubulaire
Creuset avec couvercle (porcelaine)Creuset avec couvercle (porcelaine)
Gants résistants à la chaleurGants résistants à la chaleur
4

Grind 48 hours with alcohol, dry

Pulverise the pre-fired material in a ball mill with alcohol for 48 hours, then dry it. This is the pre-fired powder.

Outils nécessaires :

Broyeur à boulets de ferBroyeur à boulets de fer
Éthanol de laboratoire, 95 %Éthanol de laboratoire, 95 %
Étuve de séchageÉtuve de séchage
5

Stir into 8 % polyvinyl acetate in acetone

Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.

Outils nécessaires :

Polyacétate de vinylePolyacétate de vinyle
AcétoneAcétone
Balance à fléauBalance à fléau
6

Mould without a first field

Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.

Outils nécessaires :

Matrice de pressage de disquesMatrice de pressage de disques
Presse hydrauliquePresse hydraulique
7

Heat to 500 °C in a 2000 oersted field

Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.

Outils nécessaires :

Four tubulaireFour tubulaire
ÉlectroaimantÉlectroaimant
Gants résistants à la chaleurGants résistants à la chaleur
8

Sinter: through a 1280 °C zone in 5 minutes

Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.

Outils nécessaires :

Four tubulaireFour tubulaire
Gants résistants à la chaleurGants résistants à la chaleur
9

Magnetise the block

Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.

Outils nécessaires :

ÉlectroaimantÉlectroaimant
BoussoleBoussole

Matériaux

2

Outils requis

15

Ce plan fabrique

Thumbnail
Espace réservé

Aimant disque

Free

2
0
1

Blueprints liés

Ces blueprints partagent des connaissances — techniques, matériaux ou principes

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

par CharlieDE

Industriel

1
0
0
0
0
0

CC0 Domaine public

Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.

Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.

Commentaires

(0)

Se connecter pour participer à la discussion

Chargement des commentaires...