Metal Oxide Varistor: Zinc Oxide with 0.05 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 99.95 % zinc oxide with 0.05 % manganese dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 96 at 1 mA and a nonlinearity exponent n of 8.4.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Avancé
2 days
Consignes
1
1
Weigh 99.95 : 0.05 and wet-mill 5 hours
Weigh 99.95 : 0.05 and wet-mill 5 hours
Mix zinc oxide and manganese dioxide 99.95 : 0.05 by moles. Ours, for 10 g: 9.995 g zinc oxide and 0.005 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Matériaux pour cette étape :
Poudre d'oxyde de zinc9.995 g
Dioxyde de manganèse (pyrolusite)0.005 gOutils nécessaires :
Balance à fléau
Broyeur à boulets de fer
Étuve de séchage2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Outils nécessaires :
Presse hydraulique
Matrice de pressage de disques
Pied à coulisse3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Outils nécessaires :
Four à moufle4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Outils nécessaires :
Grains de carbure de siliciumPied à coulisse5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Matériaux pour cette étape :
Oxyde de bismuth1 as requiredOutils nécessaires :
Résine époxy
n-ButanolFour à moufle6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Matériaux pour cette étape :
Lingot d'aluminium1 as required
Peinture conductrice à l'argent1 as required
Fil de cuivre2 piècesOutils nécessaires :
Méthode de projection de métal inconnuePied à coulisseMatériaux
6- 9.995 gEspace réservé
- Espace réservé
- 1 as requiredEspace réservé
- 1 as requiredEspace réservé
- 1 as requiredEspace réservé
- 2 piècesEspace réservé
Outils requis
11- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
Blueprints liés
Ces blueprints partagent des connaissances — techniques, matériaux ou principes
CC0 Domaine public
Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.
Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.