Barium-Calcium Ferrite Disc Magnet: Equal Barium and Calcium, Sintered at 1280 °C (Went, Philips 1956, Ex. 22)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
0
0
0
0
0

Barium-Calcium Ferrite Disc Magnet: Equal Barium and Calcium, Sintered at 1280 °C (Went, Philips 1956, Ex. 22)

A ceramic magnet with equal parts barium and calcium: 0.3 mol barium carbonate, 0.3 mol calcium carbonate and 3.1 mol iron oxide, milled 15 hours, pressed and passed through a 1280 °C furnace in 10 minutes, with no presintering. Went's rod held 1,595 gauss with a coercive force of 1,890 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 22. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lanjutan
2 days

Instruksi

1

Weigh barium carbonate, chalk and iron oxide

Weigh 59.5 g barium carbonate (0.3 mol), 30.2 g calcium carbonate (0.3 mol) and 500.0 g ferric oxide (3.1 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Material untuk langkah ini:

Barium karbonat (witherit)Barium karbonat (witherit)59.5 g
Kalsium karbonat (kapur tulis halus)Kalsium karbonat (kapur tulis halus)30.2 g
Besi(III) OksidaBesi(III) Oksida500 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Sarung tangan karetSarung tangan karet
Respirator P100Respirator P100
2

Mill with alcohol 15 hours, dry, press

Grind with alcohol in a ball mill for 15 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods). No presintering.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Etanol mutu laboratorium, 95 %Etanol mutu laboratorium, 95 %
Oven pengeringanOven pengeringan
Mesin pres hidrolikMesin pres hidrolik
Cetakan press cakramCetakan press cakram
3

Pass through a 1280 °C zone in 10 minutes

Sinter at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas
4

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Alat yang dibutuhkan:

ElektromagnetElektromagnet
KompasKompas

Bahan

3

Alat yang Diperlukan

12

Cetak biru ini membuat

Thumbnail
Placeholder

Magnet Cakram

Free

1
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

oleh CharlieDE

Industri

1
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.