Barium-Strontium Ferrite Disc Magnet: 0.21 mol BaCO3, 0.09 mol SrCO3, 1300 °C (Went, Philips 1956, Ex. 30)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
1
0
0
0
0

Barium-Strontium Ferrite Disc Magnet: 0.21 mol BaCO3, 0.09 mol SrCO3, 1300 °C (Went, Philips 1956, Ex. 30)

A ceramic magnet with both barium and strontium: 0.21 mol barium carbonate and 0.09 mol strontium carbonate to 2.7 mol iron oxide, milled as in Example 28, pressed and passed through a 1300 °C furnace in 10 minutes. Went's rod held 1,245 gauss with a coercive force of 2,370 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 30. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lanjutan
2 days

Instruksi

1

Weigh the carbonates and iron oxide

Weigh 41.7 g barium carbonate (0.21 mol), 13.3 g strontium carbonate (0.09 mol), 435.5 g ferric oxide (2.7 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Material untuk langkah ini:

Barium karbonat (witherit)Barium karbonat (witherit)41.7 g
Stronsium karbonatStronsium karbonat13.3 g
Besi(III) OksidaBesi(III) Oksida435.5 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Sarung tangan karetSarung tangan karet
Respirator P100Respirator P100
2

Mill with alcohol 15 hours, dry

As in Example 28: grind the mixture with alcohol in a ball mill for 15 hours, then dry it.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Etanol mutu laboratorium, 95 %Etanol mutu laboratorium, 95 %
Oven pengeringanOven pengeringan
3

Press the powder

Example 28 moulds a rod without giving the pressure. Ours: press discs at 1.5 tonnes per cm², the pressure of the patent's other examples.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan press cakramCetakan press cakram
4

Pass through a 1300 °C zone in 10 minutes

Sinter in air at 1300 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Alat yang dibutuhkan:

ElektromagnetElektromagnet
KompasKompas

Bahan

3

Alat yang Diperlukan

12

Cetak biru ini membuat

Thumbnail
Placeholder

Magnet Cakram

Free

2
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

oleh CharlieDE

Industri

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

oleh CharlieDE

Industri

4
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...