Ferrite Toroid Core: Magnesium-Zinc Ferrite Reheated 18 h at 1000 °C and 20 h at 750 °C (Snoek 1948, Ex. III)
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
2
0
0
0
0

Ferrite Toroid Core: Magnesium-Zinc Ferrite Reheated 18 h at 1000 °C and 20 h at 750 °C (Snoek 1948, Ex. III)

Snoek's magnesium-zinc ferrite ring (Example III), fired at 1400 °C and then given a second long treatment in oxygen: 18 hours at 1000 °C and 20 hours at 750 °C. He measured how its losses change with frequency, but gives no permeability for the reheated core. Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example III. Picture: our diagram.
Lanjutan
3 days

Instruksi

1

Weigh 28 : 18 : 54 mol %

Mix 28 mol % magnesium oxide, 18 mol % zinc oxide and 54 mol % ferric oxide. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.

Material untuk langkah ini:

Magnesium oksidaMagnesium oksida10.06 g
Serbuk Seng OksidaSerbuk Seng Oksida13.06 g
Besi(III) OksidaBesi(III) Oksida76.88 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Masker DebuMasker Debu
2

Grind 30 hours in an iron mill

Grind the mixture for 30 hours in an iron ball mill.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Masker DebuMasker Debu
3

Mould a ring at 4 tons per cm²

Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan Penekan CincinCetakan Penekan Cincin
Masker DebuMasker Debu
4

Fire 2 hours at 1400 °C, cool 5–10 °C a minute

Heat the ring in oxygen for 2 hours at 1400 °C and cool it slowly in oxygen at 5 to 10 °C per minute.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas
5

Reheat: 18 hours at 1000 °C, 20 hours at 750 °C

Heat the cooled core to 1000 °C and hold it there for 18 hours, then at 750 °C for 20 hours, and cool slowly again, all in oxygen. Snoek shows the resulting losses only as a curve; he gives no permeability for it.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas

Bahan

3

Alat yang Diperlukan

11

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

251
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)

Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)

oleh CharlieDE

Industri

8
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...