Strontium Ferrite Disc Magnet: 0.4 mol SrCO3 to 3.6 mol Iron Oxide, 1270 °C (Went, Philips 1956, Ex. 14)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
0
0
0
0
0

Strontium Ferrite Disc Magnet: 0.4 mol SrCO3 to 3.6 mol Iron Oxide, 1270 °C (Went, Philips 1956, Ex. 14)

A ceramic magnet with strontium in place of barium: 0.4 mol strontium carbonate to 3.6 mol iron oxide, milled 15 hours and passed through a 1270 °C furnace in 20 minutes. Went's rod held 1,290 gauss with a coercive force of 3,080 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 14. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lanjutan
2 days

Instruksi

1

Weigh strontium carbonate and iron oxide

Weigh 59.1 g strontium carbonate (0.4 mol) and 580.0 g ferric oxide (3.6 mol).

Material untuk langkah ini:

Stronsium karbonatStronsium karbonat59.1 g
Besi(III) OksidaBesi(III) Oksida580 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Respirator P100Respirator P100
2

Mill with alcohol 15 hours and dry

Grind with alcohol in a ball mill for 15 hours and dry.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Etanol mutu laboratorium, 95 %Etanol mutu laboratorium, 95 %
Oven pengeringanOven pengeringan
3

Form the pieces and dry overnight

The patent extrudes rods; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry overnight.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan press cakramCetakan press cakram
Oven pengeringanOven pengeringan
4

Pass through a 1270 °C zone in 20 minutes

Sinter in air at 1270 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Alat yang dibutuhkan:

ElektromagnetElektromagnet
KompasKompas

Bahan

2

Alat yang Diperlukan

11

Cetak biru ini membuat

Thumbnail
Placeholder

Magnet Cakram

Free

1
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

oleh CharlieDE

Industri

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

oleh CharlieDE

Industri

2
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...