Barium Ferrite Disc Magnet: Example 2 Without the Orienting Field (Gorter, Philips 1956, Ex. 2 Comparison)
A ceramic magnet from pre-fired barium ferrite powder suspended in polyvinyl acetate in acetone, made as in Example 2 but without the first, orienting field. Made without the first field, Gorter's comparison block reached a (BH)max of only 0.8 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 2. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
پیشرفته
3 days
دستورالعمل‌ها
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
مواد مورد نیاز این مرحله:
کربنات باریم (ویتریت)450 گرم
اکسید فریک2000 گرمابزارهای مورد نیاز:
ترازوی دو کفه
دستکش لاستیکی
ماسک تنفسی P1002
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
ابزارهای مورد نیاز:
آسیاب گلوله‌ای آهنی
اتانول - درجهٔ آزمایشگاهی، 95 %
کورهٔ خشک‌کردن3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
ابزارهای مورد نیاز:
کورهٔ لوله‌ای
بوته با درپوش (چینی)
دستکش گرمااستوار4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
ابزارهای مورد نیاز:
آسیاب گلوله‌ای آهنیاتانول - درجهٔ آزمایشگاهی، 95 %کورهٔ خشک‌کردن5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 4 cc of solution per 3 g of powder. The binder burns off later.
ابزارهای مورد نیاز:
پلی‌وینیل استات
استونترازوی دو کفه6
6
Mould without a first field
Mould without a first field
Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.
ابزارهای مورد نیاز:
قالب پرس دیسک
پرس هیدرولیک7
7
Compress into a block
Compress into a block
Compress the powder into a block. The pressure is not given.
ابزارهای مورد نیاز:
پرس هیدرولیکقالب پرس دیسک8
8
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
ابزارهای مورد نیاز:
کورهٔ لوله‌ای
آهنربای برقیدستکش گرمااستوار9
9
Sinter: through a 1300 °C zone in 5 minutes
Sinter: through a 1300 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1300 °C with a 10 cm hot zone: about 5 minutes in the heat.
ابزارهای مورد نیاز:
کورهٔ لولهایدستکش گرمااستوار10
10
Magnetise the block
Magnetise the block
Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.
ابزارهای مورد نیاز:
آهنربای برقی
قطبنمامواد
2- 450 گرمجایگزین
- 2000 گرمجایگزین
ابزارهای لازم
15- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
- جایگزین
این نقشه می‌سازد
نقشه‌های مرتبط
این نقشه‌ها دانش مشترکی دارند — تکنیک‌ها، مواد یا اصول
CC0 مالکیت عمومی
این نقشه تحت مجوز CC0 منتشر شده است. شما آزاد هستید آن را کپی، ویرایش، توزیع و برای هر هدفی بدون نیاز به اجازه استفاده کنید.
با خرید محصولات از طریق نقشه از سازنده حمایت کنید و او کمیسیون سازنده تعیین شده توسط فروشندگان، دریافت می‌کند یا یک نسخه جدید از این نقشه ایجاد کنید و آن را به عنوان اتصال در نقشه خود قرار دهید تا درآمد به اشتراک گذاشته شود.