Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)
Charlie

Creato da

Charlie

21. ottobre 2026DE
1
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this copper-zinc ferrite ring at a lower heat: technical copper oxide, zinc oxide and iron oxide with 1 % brownstone, fired at 1050 °C, then held 14 hours at 600 °C, all in oxygen. His ring had an initial permeability of 385. The picture: our diagram.
Avanzato
2 days

Istruzioni

1

Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone

Mix technical copper oxide, zinc oxide and iron oxide in the molecular ratio 20.7 : 31.6 : 47.7 (on the pure oxides) and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.91 g copper oxide, 21.73 g zinc oxide and 64.36 g ferric oxide per 100 g, plus 1 g brownstone.

Materiali per questo passaggio:

Ossido di rameOssido di rame13.91 g
Polvere di ossido di zincoPolvere di ossido di zinco21.73 g
Ossido ferricoOssido ferrico64.36 g
Biossido di manganese (pirolusite)Biossido di manganese (pirolusite)1 g

Strumenti necessari:

Bilancia a bracciBilancia a bracci
Mascherina antipolvereMascherina antipolvere
2

Grind for 3 hours in an iron ball mill

Grind the mixture for 3 hours in a mill with iron balls.

Strumenti necessari:

Mulino a sfere di ferroMulino a sfere di ferro
Mascherina antipolvereMascherina antipolvere
3

Mould a ring at 4 tons per cm²

Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.

Strumenti necessari:

Pressa idraulicaPressa idraulica
Stampo di pressatura ad anelloStampo di pressatura ad anello
Acqua distillataAcqua distillata
4

Fire 1 hour at 1050 °C, hold 14 hours at 600 °C

Sinter the ring in oxygen at 1050 °C for 1 hour, cool it slowly to 600 °C and hold it there for 14 hours, all in oxygen, then let it cool further. Snoek's core had an initial permeability of 385.

Strumenti necessari:

Forno a tuboForno a tubo
OssigenoOssigeno
Bombola di gas in pressioneBombola di gas in pressione
PirometroPirometro
Tenaglia per crogioloTenaglia per crogiolo
Guanti resistenti al caloreGuanti resistenti al calore

Materiali

4

Strumenti richiesti

12

Questo progetto realizza

Thumbnail
Segnaposto

Nucleo toroidale di ferrite

Free

249
0
1

Blueprint correlati

Questi blueprint condividono conoscenze — tecniche, materiali o principi

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Pericoloso

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

di CharlieDE

Industriale

3
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

di CharlieDE

Inorganico

0
0
0
0
0
0
Copper(II) Oxide by Heating Copper in Air

Copper(II) Oxide by Heating Copper in Air

di CharlieDE

Chimica

14
0
0
0
0
0

CC0 Pubblico dominio

Questo progetto è rilasciato sotto CC0. Sei libero di copiare, modificare, distribuire e utilizzare quest'opera per qualsiasi scopo, senza chiedere permesso.

Supporta il Maker acquistando prodotti tramite il suo progetto dove guadagna una Commissione Maker stabilita dai venditori, oppure crea una nuova iterazione di questo progetto e includilo come collegamento nel tuo progetto per condividere i ricavi.

Commenti

(0)

Accedi per partecipare alla discussione

Caricamento commenti...