Hammering Bronze Sheet from a Cast Ingot — Raising and Planishing
Forge

作成者

Forge

26. 5月 2026NO
14
0
0
0
0

Hammering Bronze Sheet from a Cast Ingot — Raising and Planishing

Sheet bronze was the material behind Bronze Age armour, vessels, mirrors, and decorative work. Unlike casting which produces a fixed shape, sheet-working starts with a flat ingot and transforms it through repeated cycles of hammering and annealing into sheets as thin as 0.5 mm — thinner than modern cardboard.

The process exploits a fundamental property of bronze: cold-hammering compresses the crystal grains, making the metal harder and thinner with each blow. But this work-hardening also makes the bronze brittle. Before it cracks, the smith heats it to dull red (annealing), which recrystallises the grain structure and restores ductility. A single ingot may go through 10-15 anneal-hammer cycles to reach usable sheet thickness.

The finished sheet can then be cut, bent, raised into vessels, riveted, engraved, or embossed — opening the full range of Bronze Age metalcraft.

中級者
3-5 hours (multiple anneal-hammer cycles)

手順

1

Cast a flat ingot

Pour molten bronze into a shallow rectangular depression carved in a flat stone slab — approximately 15 cm long, 8 cm wide, and 1.5 cm deep. Allow to cool completely. The resulting ingot is the raw stock for sheet-working. A rougher ingot works fine; the hammering process will refine the surface.

このステップの材料:

Copper Sheet (0.5-1mm)Copper Sheet (0.5-1mm)500 g
2

Set up the anvil stone

Select the flattest, hardest stone available — granite or dense river cobble. The anvil surface must be larger than the ingot and as smooth as possible. Every dent in the anvil transfers to the sheet as a raised bump. Bed the stone firmly in packed earth so it does not shift during hammering.

必要な工具:

Flat Stone SlabFlat Stone Slab
3

First hammering pass — rough thinning

Place the ingot on the anvil. Using a smooth-faced hammerstone, strike the ingot with firm, overlapping blows in straight rows across the entire surface. Always work in one direction per pass, then rotate the ingot 90 degrees for the next pass. This cross-hammering prevents the metal from stretching unevenly. After 100-150 blows the ingot noticeably thins and spreads.

必要な工具:

HammerstoneHammerstone
4

First anneal

The ingot is now work-hardened and resists further hammering. Place it in a charcoal fire and heat until it glows dull cherry red throughout — about 500-600 °C. Remove with tongs and let cool in still air. The bronze is now soft again. Do not quench in water; rapid cooling does not harden bronze (unlike steel) but can cause thermal shock cracking in thick sections.

このステップの材料:

CharcoalCharcoal2 kg

必要な工具:

Long-Handled TongsLong-Handled Tongs
5

Continue hammer-anneal cycles

Repeat the hammering and annealing cycle. Each cycle reduces the thickness by roughly 30-40%. Track your progress: starting from 15 mm thick ingot, after cycle 1 you reach about 10 mm, cycle 2 about 6 mm, cycle 3 about 4 mm, and so on. The sheet grows wider and longer with each pass. Trim ragged edges with a sharp flint flake between cycles.
6

Detect and prevent edge cracking

After each anneal, inspect the sheet edges carefully. Small cracks appear at the edges first because the thinner edges work-harden faster than the centre. If you see cracks forming, trim them immediately with a flint cutter before the next hammering pass — a crack that propagates into the sheet body ruins the entire piece. Anneal more frequently near the end when the sheet is thin.
7

Final thinning to usable sheet

After 8-12 anneal-hammer cycles, the sheet should be 1-2 mm thick — suitable for vessels, armour, and decorative work. For mirrors or ornaments, continue to 0.5-0.8 mm. At this thickness the bronze becomes semi-transparent when held to bright light. Each blow must be lighter and more precise — over-striking creates thin spots that tear.
8

Planish the surface

Anneal the finished sheet one final time. Then, using the smoothest stone available, strike the entire surface with very light, rapid, overlapping blows. This planishing pass does not thin the sheet further — it removes the visible hammer marks from the thinning passes and leaves a smooth, uniform surface. Work systematically in rows so no area is missed.

必要な工具:

Smooth StoneSmooth Stone
9

Polish (optional)

For mirrors or decorative pieces, rub the planished sheet with progressively finer abrasives — coarse sand, then fine sand, then wet clay on a leather pad. Bronze polishes to a mirror finish that reflects an image clearly. The ancient Egyptians used this method for hand mirrors. A final rub with animal fat protects the surface from tarnishing.

このステップの材料:

Fine SandFine Sand100 g

材料

3

必要な工具

4

接続ブループリントの材料

関連ブループリント

これらのブループリントは知識を共有しています — 技術、材料、原理

Casting a Bronze Flat Axe — The First Metal Cutting ToolForge著
Making a Clay Crucible for Smelting — The Vessel That Holds Molten MetalForge著
Making a Bronze Needle — Drawing and Hammering Fine WireForge著

CC0 パブリックドメイン

このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。

メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。

ディスカッション

(0)

ログイン してディスカッションに参加

コメントを読み込み中...