High-Speed Steel, Charge 3: Crucible-Melted Tungsten-Chrome-Molybdenum-Vanadium Steel (Carnegie & Gladwyn 1918)
High-speed steel holds its edge when it is cutting hot. In Sheffield it was made like other crucible tool steel: the best Swedish bar iron melted in small clay pots in a coke fire, with tungsten, chromium, molybdenum and vanadium added to the liquid iron. This is the third of three typical charges given by Carnegie and Gladwyn: 55 lb iron, 26 lb tungsten powder, 12 lb ferro-chrome, 9.5 lb ferro-molybdenum and 1 lb ferro-vanadium for 100 lb of steel.
Source: D. Carnegie and S. C. Gladwyn, Liquid Steel (1918), pp. 74-77, 106-107 and 113. Unknown: how the Swedish iron, the tungsten powder, the ferro-molybdenum and the ferro-vanadium are made; the melting time; and how the ingot is worked into bar. The book stops at the liquid steel, so these are linked to unknown heads. Picture: the book's Fig. 29, crucible furnaces at Samuel Osborn & Co., Sheffield.
エキスパート
1 day
手順
1
1
Weigh charge 3
Weigh charge 3
For 100 lb of steel: 55 lb best Swedish bar iron, cut up; 26 lb tungsten powder (96 to 98 % tungsten); 12 lb ferro-chrome (60 % chromium); 9.5 lb ferro-molybdenum (80 % molybdenum); 1.0 lb ferro-vanadium (35 to 40 % vanadium). Unknown: how the Swedish iron, tungsten powder, ferro-molybdenum and ferro-vanadium are made. The book only lists them.
このステップの材料:
スウェーデン棒鉄55 ポンド
タングステン粉26 ポンド
フェロクロム12 ポンド
フェロモリブデン9.5 ポンド
フェロバナジウム1 ポンド必要な工具:
天秤ばかり2
2
Set two clay crucibles in the melting hole
Set two clay crucibles in the melting hole
Tool steels are melted in small crucibles, about 55 lb each, two to a hole in a Huntsman coke furnace (ours: the 100 lb charge split between the two). Stand them on fireclay stands on the fire bars, straight from the annealing furnace, and fill the hole with coke up to their tops. Use the best washed coke, as free from sulphur as possible: sulphur gets into the steel even through the lid. When the pots are white hot, throw in a little sand to fuse them onto their stands.
必要な工具:
るつぼ炉
耐火粘土のるつぼ
冶金用コークス
砂
るつぼばさみ3
3
Melt the iron, then add the alloys
Melt the iron, then add the alloys
Charge the cut iron, put on the clay lids, fill the hole with coke and close the cover. Renew the fire as it burns through. Add the tungsten powder and ferro-alloys to the liquid iron and melt them in. Unknown: the melting time and temperature for this charge. The book says only that tool steel takes longer than ordinary steel. About 3½ tons of coke go to each ton of high-speed steel.
必要な工具:
るつぼ炉冶金用コークスるつぼばさみ4
4
Pull out, skim and teem
Pull out, skim and teem
Lift each pot out with the pulling-out tongs (arms and legs covered with wet sacking), take off the lid and skim the slag with a mop, then pour the steel into ingot moulds. Unknown: the ingot size. A clay crucible lasts about 3 heats.
必要な工具:
るつぼばさみ
インゴット鋳型
耐熱手袋5
5
Work the ingot into round bar
Work the ingot into round bar
Unknown: how the ingot is heated, hammered or rolled, and annealed into round bar. Carnegie and Gladwyn stop at the liquid steel, so this step is linked to an unknown head until a source gives it.
必要な工具:
不明な鍛造工程材料
5- 55 ポンドプレースホルダー
- 26 ポンドプレースホルダー
- 12 ポンドプレースホルダー
- 9.5 ポンドプレースホルダー
- 1 ポンドプレースホルダー
この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
Crucible Cast Steel by the Huntsman Process — Remelting Blister Steel into Flawless Ingots
Tarkin 作
金属加工
58
0
0
0
0
0
危険
Ductile Tungsten Wire: Pressed, Sintered by Current, Swaged and Drawn Hot (Coolidge 1913)
Forge 作
金属加工
10
0
0
0
0
0
High-Speed Steel, Charge 1: Crucible-Melted Tungsten-Chrome-Molybdenum Steel (Carnegie & Gladwyn 1918)
Forge 作
金属加工
9
0
0
0
0
0
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。