Screwdrivers: Drawn Wire, Cold-Formed Tips and Turned Handles
A screwdriver's shaft, or bar, starts as coiled steel wire drawn to size and annealed, about 1,350 °F (732 °C) for 12 hours. It is straightened and fed to a cold-forming press that cuts it to length and forms the tip and the "wings" that lock into the handle; Phillips tips have their four grooves cut in a separate operation. The bars are hardened in an in-line furnace at about 1,555 °F (846 °C), dropped into an oil quench and tempered at 450–500 °F (about 230–260 °C), then nickel-plated. Handles are usually cellulose acetate, extruded into bars, turned to shape and drilled, and the bar is pressed hydraulically into the handle.
上級者
Factory process
手順
1
1
Draw and anneal the wire
Draw and anneal the wire
Draw the coiled wire to the shaft diameter and anneal it at about 1,350 °F (732 °C) for 12 hours.
このステップの材料:
鋼線材コイル1 as required必要な工具:
連続伸線機
焼きなまし炉2
2
Cold-form
Cold-form
Straighten the wire and cold-form each bar: cut to length, form the tip and the wings that key into the handle.
必要な工具:
冷間成形プレス3
3
Harden and temper
Harden and temper
Heat the bars in an in-line furnace at about 1,555 °F (846 °C), drop them into oil, then temper them at 450–500 °F.
必要な工具:
油焼入れ付き連続焼入れ炉
焼戻し炉4
4
Plate
Plate
Nickel-plate the bars against rust.
このステップの材料:
ニッケル1 as required5
5
Make the handles
Make the handles
Extrude cellulose acetate into bars, turn the handles to shape and drill them.
このステップの材料:
酢酸セルロースペレット1 as required必要な工具:
自動旋盤6
6
Assemble
Assemble
Press each bar hydraulically into its handle.
必要な工具:
油圧組立プレスこの設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。