Aqueous PTFE Dispersion: Tetrafluoroethylene Polymerised in Soapy Water (Berry 1951)
Ordinary soaps stop tetrafluoroethylene from growing into long chains. A fluorine soap does not: with 2 % of ammonium dodecafluoroheptanoate in the water, the gas polymerises into tiny PTFE ribbons that stay suspended. The result is a milky dispersion, a third of it polymer, the raw material for PTFE fine powder.
Source: K. L. Berry (du Pont), US 2,559,752 (1951), Example III. Making the ammonium salt from our acid, and the apparatus, are ours. Picture drawn by Youblob.
Juu
1 day
Maagizo
1
1
Make the ammonium salt
Make the ammonium salt
Ours: neutralise about 1.9 parts of dodecafluoroheptanoic acid with ammonia solution until just neutral to litmus, giving 2 parts of ammonium dodecafluoroheptanoate. Make it up with distilled water to 93 parts of water in all. Parts are by weight.
Vifaa kwa hatua hii:
Asidi ya dodekafluoroheptanoiki1.9 parts
Myeyusho wa amonia - asilimia 25-281 as required to neutralise
Maji yaliyosafishwa kwa mvuke93 partsZana zinazohitajika:
Karatasi ya litmasi
Chombo cha kioo
Mizani ya mizani-mbili2
2
Load the pressure vessel
Load the pressure vessel
Put the solution in a pressure vessel with 0.05 part of potassium persulfate and 5 parts of paraffin wax melting at 56–58 °C. The wax protects the colloid while it is stirred.
Zana zinazohitajika:
Kianzishi cha persulfati
Nta ya parafini
Riakta ya shinikizoMizani ya mizani-mbili3
3
Heat and remove the air
Heat and remove the air
Bring it to 80–85 °C, then evacuate the vessel and hold it under reduced pressure for several minutes to drive out air and dissolved oxygen.
Zana zinazohitajika:
Riakta ya shinikizo
Pampu ya utupu
Kipimajoto4
4
Feed tetrafluoroethylene for 3.6 hours
Feed tetrafluoroethylene for 3.6 hours
Let in tetrafluoroethylene to 60 lb/sq in gauge. Agitate at 80–85 °C for 3.6 hours; each time the pressure falls to 55 lb/sq in, bring it back to 60.
Vifaa kwa hatua hii:
Tetrafluoroethilini1 as required to hold 55–60 psiZana zinazohitajika:
Riakta ya shinikizo
Mtungi wa gesi yenye shinikizo
Kipima ShinikizoKipimajoto5
5
Cool and lift off the wax
Cool and lift off the wax
Cool it. The paraffin sets on top and lifts off. Below it is a colloidal PTFE dispersion with 34 % solids.
Zana zinazohitajika:
Riakta ya shinikizo
Mitungi ya kioo yenye vifunikoVifaa
4- 1.9 partsKishikilia Nafasi
- 1 as required to neutraliseKishikilia Nafasi
- 93 partsKishikilia Nafasi
- 1 as required to hold 55–60 psiKishikilia Nafasi
Zana Zinazohitajika
11- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- 1 vendor sell this, none ship to you yetKishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
Mchoro huu unatengeneza
Blueprint zinazohusiana
Blueprint hizi zinashiriki maarifa — mbinu, vifaa au kanuni
Hatari
Dodecafluoroheptanoic Acid: the Fluoro Alcohol Oxidised with Permanganate (Berry 1951)
na Charlie
Viwandani
3
0
0
0
0
0
Hatari
Tetrafluoroethylene: Chlorodifluoromethane Pyrolysed in a Silver Tube at 700 °C
na Charlie
Viwandani
9
0
0
0
0
0
PTFE Resin Powder: Tetrafluoroethylene Polymerised under Pressure, Plunkett 1941
na Charlie
Viwandani
5
0
0
0
0
0
CC0 Umma Wote
Mchoro huu umetolewa chini ya CC0. Uko huru kunakili, kubadilisha, kusambaza, na kutumia kazi hii kwa madhumuni yoyote, bila kuomba ruhusa.
Saidia Mtengenezaji kwa kununua bidhaa kupitia Mchoro wao ambapo wanapata Kamisheni ya Mtengenezaji iliyowekwa na Wachuuzi, au unda marudio mapya ya Mchoro huu na uiunganishe kama kiungo katika Mchoro wako kuchangia mapato.