Barium Ferrite Disc Magnet, Sintered at 1200 °C (Went, Philips 1956)
The dark grey ceramic magnet on fridges and in loudspeakers is barium ferrite. It is made from two cheap powders: one part barium carbonate to six of iron oxide, milled, fired, milled again, pressed and sintered. No cobalt or nickel is needed. This is Example 34 of the Philips patent. This iteration sinters at 1200 °C, where his rod held 1,400 gauss with a coercive force of 3,100 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956). They pressed rods; the claim covers "a body of a desired shape", and the disc size is ours. The patent does not say how to magnetise it; our way is stated. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
កម្រិតខ្ពស់
2 days
ការណែនាំ
1
1
Weigh one part barium carbonate to six of iron oxide
Weigh one part barium carbonate to six of iron oxide
Weigh 39.5 g of barium carbonate (0.2 mol) and 191.7 g of ferric oxide, Fe2O3 (1.2 mol). Barium carbonate is poisonous if swallowed: ours, gloves and a dust respirator.
សម្ភារៈសម្រាប់ជំហាននេះ៖
កាបូណាតបារីយ៉ូម (វីធើរីត)39.5 ក្រ
អុកស៊ីដហ្វែរិក191.7 ក្រឧបករណ៍ដែលត្រូវការ៖
ជញ្ជីងចានពីរ
ស្រោមដៃកៅស៊ូ
ម៉ាស់ការពារផ្លូវដង្ហើម P1002
2
Mill with ethanol for 4 hours
Mill with ethanol for 4 hours
Grind the mixture with ethanol in an iron ball mill for 4 hours. Let the ethanol evaporate, then dry the powder in a drying oven.
ឧបករណ៍ដែលត្រូវការ៖
ម៉ាស៊ីនកិនគ្រាប់ដែក
អេតាណុល - ថ្នាក់មន្ទីរពិសោធន៍, 95 %
ឡសម្ងួត3
3
Presinter at 1000 °C for 4 hours
Presinter at 1000 °C for 4 hours
Fire the dry powder in air at 1000 °C for 4 hours (ours: in a lidded porcelain crucible in a muffle furnace). Let it cool.
ឧបករណ៍ដែលត្រូវការ៖
ឡដុតមូហ្វល
ចានរលាយមានគម្រប (ព័រសឺឡែន)
ដង្កាប់ឆ្នាំងរំលាយ
ស្រោមដៃធន់កម្តៅ4
4
Mill again for 4 hours
Mill again for 4 hours
Grind the presintered product with ethanol in the ball mill for another 4 hours. Let the ethanol evaporate.
ឧបករណ៍ដែលត្រូវការ៖
ម៉ាស៊ីនកិនគ្រាប់ដែកអេតាណុល - ថ្នាក់មន្ទីរពិសោធន៍, 95 %ឡសម្ងួតម៉ាស់ការពារផ្លូវដង្ហើម P1005
5
Press discs at 1.5 tons per cm²
Press discs at 1.5 tons per cm²
Press the powder at 1.5 tons/cm². The patent pressed rods; we press discs. Ours: a die 20 mm across, so about 4.7 tonnes on the punch (our arithmetic: 1.5 × 3.14 cm²).
ឧបករណ៍ដែលត្រូវការ៖
ម៉ាស៊ីនសង្កត់អ៊ីដ្រូលិក
ពុម្ពសង្កត់ថាស6
6
Sinter 4 hours at 1200 °C
Sinter 4 hours at 1200 °C
Sinter the discs for 4 hours at 1200 °C in oxygen or in air. The patent's rod at 1200 °C: 1,400 gauss and 3,100 oersted.
ឧបករណ៍ដែលត្រូវការ៖
ឡដុតមូហ្វលដង្កាប់ឆ្នាំងរំលាយស្រោមដៃធន់កម្តៅ7
7
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
ឧបករណ៍ដែលត្រូវការ៖
អេឡិចត្រូម៉ាញេទិច
ត្រីវិស័យសម្ភារៈ
2- 39.5 ក្រកន្លែងទុក
- 191.7 ក្រកន្លែងទុក
ឧបករណ៍ចាំបាច់
14- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
ប្លង់នេះធ្វើ
ប្លង់ពាក់ព័ន្ធ
ប្លង់ទាំងនេះចែករំលែកចំណេះដឹង — បច្ចេកទេស សម្ភារៈ ឬគោលការណ៍
Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)
ដោយ Charlie
ឧស្សាហកម្ម
1
0
0
0
0
0
គ្រោះថ្នាក់
Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
ដោយ Charlie
ឧស្សាហកម្ម
13
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated
ដោយ Charlie
គ្មានកាបូន
8
0
0
0
0
0
CC0 សាធារណៈ
ប្លង់នេះត្រូវបានចេញផ្សាយក្រោម CC0។ អ្នកមានសិទ្ធិចម្លង កែប្រែ ចែកចាយ និងប្រើប្រាស់ដោយមិនចាំបាច់សុំអនុញ្ញាត។
គាំទ្រអ្នកបង្កើតដោយទិញផលិតផលតាមរយៈប្លង់របស់ពួកគេ ដែលពួកគេទទួលបាន កម្រៃជើងសារអ្នកបង្កើត កំណត់ដោយអ្នកលក់ ឬបង្កើតកំណែថ្មីនៃប្លង់នេះ ហើយបញ្ចូលជាការតភ្ជាប់ក្នុងប្លង់របស់អ្នកដើម្បីចែករំលែកចំណូល។