Oriented Barium Ferrite Disc Magnet: Powder Ground 48 Hours (Gorter, Philips 1956, Ex. 7)
A ceramic magnet made as in Example 4 from pre-fired barium ferrite ground for 48 hours instead of 12. In the principal direction it held 3,100 gauss with a coercive force of 1,650 oersted and a (BH)max of 1.72 × 10⁶, the best in the patent.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 7. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
កម្រិតខ្ពស់
3 days
ការណែនាំ
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
សម្ភារៈសម្រាប់ជំហាននេះ៖
កាបូណាតបារីយ៉ូម (វីធើរីត)450 ក្រ
អុកស៊ីដហ្វែរិក2000 ក្រឧបករណ៍ដែលត្រូវការ៖
ជញ្ជីងចានពីរ
ស្រោមដៃកៅស៊ូ
ម៉ាស់ការពារផ្លូវដង្ហើម P1002
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
ឧបករណ៍ដែលត្រូវការ៖
ម៉ាស៊ីនកិនគ្រាប់ដែក
អេតាណុល - ថ្នាក់មន្ទីរពិសោធន៍, 95 %
ឡសម្ងួត3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
ឧបករណ៍ដែលត្រូវការ៖
ឡបំពង់
ចានរលាយមានគម្រប (ព័រសឺឡែន)
ស្រោមដៃធន់កម្តៅ4
4
Grind 48 hours with alcohol, dry
Grind 48 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 48 hours, then dry it. This is the pre-fired powder.
ឧបករណ៍ដែលត្រូវការ៖
ម៉ាស៊ីនកិនគ្រាប់ដែកអេតាណុល - ថ្នាក់មន្ទីរពិសោធន៍, 95 %ឡសម្ងួត5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
ឧបករណ៍ដែលត្រូវការ៖
ប៉ូលីវីនីលអាសេតាត
អាសេតូនជញ្ជីងចានពីរ6
6
Orient in a 10000 oersted field
Orient in a 10000 oersted field
Put the suspension in a moulding die between the poles of a magnet and apply a first field of 10000 oersted. Remove the binder solution while the field is on.
ឧបករណ៍ដែលត្រូវការ៖
ពុម្ពសង្កត់ថាស
អេឡិចត្រូម៉ាញេទិច
ម៉ាស៊ីនសង្កត់អ៊ីដ្រូលិក7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
ឧបករណ៍ដែលត្រូវការ៖
ឡបំពង់អេឡិចត្រូម៉ាញេទិចស្រោមដៃធន់កម្តៅ8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
ឧបករណ៍ដែលត្រូវការ៖
ឡបំពង់ស្រោមដៃធន់កម្តៅ9
9
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
ឧបករណ៍ដែលត្រូវការ៖
អេឡិចត្រូម៉ាញេទិច
ត្រីវិស័យសម្ភារៈ
2- 450 ក្រកន្លែងទុក
- 2000 ក្រកន្លែងទុក
ឧបករណ៍ចាំបាច់
15- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
ប្លង់នេះធ្វើ
ប្លង់ពាក់ព័ន្ធ
ប្លង់ទាំងនេះចែករំលែកចំណេះដឹង — បច្ចេកទេស សម្ភារៈ ឬគោលការណ៍
CC0 សាធារណៈ
ប្លង់នេះត្រូវបានចេញផ្សាយក្រោម CC0។ អ្នកមានសិទ្ធិចម្លង កែប្រែ ចែកចាយ និងប្រើប្រាស់ដោយមិនចាំបាច់សុំអនុញ្ញាត។
គាំទ្រអ្នកបង្កើតដោយទិញផលិតផលតាមរយៈប្លង់របស់ពួកគេ ដែលពួកគេទទួលបាន កម្រៃជើងសារអ្នកបង្កើត កំណត់ដោយអ្នកលក់ ឬបង្កើតកំណែថ្មីនៃប្លង់នេះ ហើយបញ្ចូលជាការតភ្ជាប់ក្នុងប្លង់របស់អ្នកដើម្បីចែករំលែកចំណូល។