Metal Oxide Varistor: Zinc Oxide with 0.05 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 99.95 % zinc oxide with 0.05 % manganese dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 96 at 1 mA and a nonlinearity exponent n of 8.4.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
កម្រិតខ្ពស់
2 days
ការណែនាំ
1
1
Weigh 99.95 : 0.05 and wet-mill 5 hours
Weigh 99.95 : 0.05 and wet-mill 5 hours
Mix zinc oxide and manganese dioxide 99.95 : 0.05 by moles. Ours, for 10 g: 9.995 g zinc oxide and 0.005 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
សម្ភារៈសម្រាប់ជំហាននេះ៖
ម្សៅស័ង្កសីអុកស៊ីត9.995 ក្រ
ម៉ង់ហ្គាណែសឌីអុកស៊ីត (ពីរ៉ូលូស៊ីត)0.005 ក្រឧបករណ៍ដែលត្រូវការ៖
ជញ្ជីងចានពីរ
ម៉ាស៊ីនកិនគ្រាប់ដែក
ឡសម្ងួត2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
ឧបករណ៍ដែលត្រូវការ៖
ម៉ាស៊ីនសង្កត់អ៊ីដ្រូលិក
ពុម្ពសង្កត់ថាស
ខ្នាតវ៉ែនញ្ញេ3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
ឧបករណ៍ដែលត្រូវការ៖
ឡដុតមូហ្វល4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
ឧបករណ៍ដែលត្រូវការ៖
គ្រាប់ស៊ីលីកូនកាបួតខ្នាតវ៉ែនញ្ញេ5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
សម្ភារៈសម្រាប់ជំហាននេះ៖
អុកស៊ីតប៊ីស្មុត1 as requiredឧបករណ៍ដែលត្រូវការ៖
អេប៉ុកស៊ីរេស៊ីន
n-ប៊ូតាណុលឡដុតមូហ្វល6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
សម្ភារៈសម្រាប់ជំហាននេះ៖
ដុំអាលុយមីញ៉ូម1 as required
ថ្នាំលាបប្រាក់ចម្លងចរន្ត1 as required
ខ្សែស្ពាន់2 ដុំឧបករណ៍ដែលត្រូវការ៖
វិធីបាញ់លោហៈដែលមិនស្គាល់ខ្នាតវ៉ែនញ្ញេសម្ភារៈ
6- 9.995 ក្រកន្លែងទុក
- 0.005 ក្រកន្លែងទុក
- 1 as requiredកន្លែងទុក
- 1 as requiredកន្លែងទុក
- 1 as requiredកន្លែងទុក
- 2 ដុំកន្លែងទុក
ឧបករណ៍ចាំបាច់
11- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
- កន្លែងទុក
ប្លង់ពាក់ព័ន្ធ
ប្លង់ទាំងនេះចែករំលែកចំណេះដឹង — បច្ចេកទេស សម្ភារៈ ឬគោលការណ៍
CC0 សាធារណៈ
ប្លង់នេះត្រូវបានចេញផ្សាយក្រោម CC0។ អ្នកមានសិទ្ធិចម្លង កែប្រែ ចែកចាយ និងប្រើប្រាស់ដោយមិនចាំបាច់សុំអនុញ្ញាត។
គាំទ្រអ្នកបង្កើតដោយទិញផលិតផលតាមរយៈប្លង់របស់ពួកគេ ដែលពួកគេទទួលបាន កម្រៃជើងសារអ្នកបង្កើត កំណត់ដោយអ្នកលក់ ឬបង្កើតកំណែថ្មីនៃប្លង់នេះ ហើយបញ្ចូលជាការតភ្ជាប់ក្នុងប្លង់របស់អ្នកដើម្បីចែករំលែកចំណូល។