Ferrite Toroid Core: Magnesium-Zinc Ferrite Reheated 18 h at 1000 °C and 20 h at 750 °C (Snoek 1948, Ex. III)
Snoek's magnesium-zinc ferrite ring (Example III), fired at 1400 °C and then given a second long treatment in oxygen: 18 hours at 1000 °C and 20 hours at 750 °C. He measured how its losses change with frequency, but gives no permeability for the reheated core.
Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example III. Picture: our diagram.
고급
3 days
안내
1
1
Weigh 28 : 18 : 54 mol %
Weigh 28 : 18 : 54 mol %
Mix 28 mol % magnesium oxide, 18 mol % zinc oxide and 54 mol % ferric oxide. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.
이 단계의 재료:
산화마그네슘10.06 g
산화아연 분말13.06 g
산화제이철76.88 g필요한 도구:
접시 저울
방진 마스크2
2
Grind 30 hours in an iron mill
Grind 30 hours in an iron mill
Grind the mixture for 30 hours in an iron ball mill.
필요한 도구:
철 볼 밀방진 마스크3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
필요한 도구:
유압 프레스
링 프레스 다이방진 마스크4
4
Fire 2 hours at 1400 °C, cool 5–10 °C a minute
Fire 2 hours at 1400 °C, cool 5–10 °C a minute
Heat the ring in oxygen for 2 hours at 1400 °C and cool it slowly in oxygen at 5 to 10 °C per minute.
필요한 도구:
관상로
산소
고압 가스통
고온계
도가니 집게
내열 장갑5
5
Reheat: 18 hours at 1000 °C, 20 hours at 750 °C
Reheat: 18 hours at 1000 °C, 20 hours at 750 °C
Heat the cooled core to 1000 °C and hold it there for 18 hours, then at 750 °C for 20 hours, and cool slowly again, all in oxygen. Snoek shows the resulting losses only as a curve; he gives no permeability for it.
필요한 도구:
관상로산소고압 가스통고온계도가니 집게내열 장갑이 블루프린트로 만드는 것
관련 블루프린트
이 블루프린트들은 지식을 공유합니다 — 기술, 재료 또는 원리
CC0 퍼블릭 도메인
이 블루프린트는 CC0로 공개되었습니다. 어떤 목적으로든 자유롭게 복사, 수정, 배포 및 사용할 수 있습니다.
제품 구매를 통해 메이커를 지원하세요. 판매자가 설정한 메이커 커미션 을 받거나, 이 블루프린트의 새로운 반복을 만들어 연결로 포함시킬 수 있습니다.