Strontium Ferrite Disc Magnet: 0.4 mol SrCO3 to 3.6 mol Iron Oxide, 1270 °C (Went, Philips 1956, Ex. 14)
A ceramic magnet with strontium in place of barium: 0.4 mol strontium carbonate to 3.6 mol iron oxide, milled 15 hours and passed through a 1270 °C furnace in 20 minutes. Went's rod held 1,290 gauss with a coercive force of 3,080 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 14. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
고급
2 days
안내
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 59.1 g strontium carbonate (0.4 mol) and 580.0 g ferric oxide (3.6 mol).
이 단계의 재료:
탄산스트론튬59.1 g
산화제이철580 g필요한 도구:
접시 저울
P100 방진 마스크2
2
Mill with alcohol 15 hours and dry
Mill with alcohol 15 hours and dry
Grind with alcohol in a ball mill for 15 hours and dry.
필요한 도구:
철 볼 밀
에탄올 - 실험실 등급, 95 %
건조 가마3
3
Form the pieces and dry overnight
Form the pieces and dry overnight
The patent extrudes rods; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry overnight.
필요한 도구:
유압 프레스
원판 압축 금형건조 가마4
4
Pass through a 1270 °C zone in 20 minutes
Pass through a 1270 °C zone in 20 minutes
Sinter in air at 1270 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.
필요한 도구:
관상로
내열 장갑5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
필요한 도구:
전자석
나침반이 블루프린트로 만드는 것
관련 블루프린트
이 블루프린트들은 지식을 공유합니다 — 기술, 재료 또는 원리
CC0 퍼블릭 도메인
이 블루프린트는 CC0로 공개되었습니다. 어떤 목적으로든 자유롭게 복사, 수정, 배포 및 사용할 수 있습니다.
제품 구매를 통해 메이커를 지원하세요. 판매자가 설정한 메이커 커미션 을 받거나, 이 블루프린트의 새로운 반복을 만들어 연결로 포함시킬 수 있습니다.